Oxidation Behavior of TiAl3/Al Composite Coating on Orthorhombic-Ti2AlNb Based Alloy at Different Temperatures

doi:10.1007/s11666-010-9473-4

IMR OpenIR

	Oxidation Behavior of TiAl3/Al Composite Coating on Orthorhombic-Ti2AlNb Based Alloy at Different Temperatures
	Kong, Lingyan; Lu, Bin; Cui, Xinyu; Du, Hao; Li, Tiefan; Xiong, Tianying
通讯作者	Kong, Lingyan(lykong@imr.ac.cn)
	2010-03-01
发表期刊	JOURNAL OF THERMAL SPRAY TECHNOLOGY
ISSN	1059-9630
卷号	19 期号:3 页码:650-656
摘要	This paper reports the oxidation behavior of TiAl3/Al composite coating deposited by cold spray. The substrate alloy was orthorhombic-Ti-22Al-26Nb (at.%). The oxidation kinetics of the coating was tested at 650, 800, and 950 A degrees C, respectively. The parabolic rate constant for the coating oxidized at 650 A degrees C was k (p) = 7.2 x 10(-2) mg center dot cm(-2)center dot h(-1/2) for the tested 1200 h. For the coating oxidized at 800 A degrees C, the oxidation kinetics could be separated into two stages with k (p) value of 39.8 x 10(-2) mg center dot cm(-2)center dot h(-1/2) for the initial 910 h and 17.7 x 10(-2) mg center dot cm(-2)center dot h(-1/2) for the stage thereafter. For the coating oxidized at 950 A degrees C, the oxidation kinetics can be separated into three stages with k (p) of 136.9 x 10(-2) mg center dot cm(-2)center dot h(-1/2) in the first 100 h, followed by 26.9 x 10(-2) mg center dot cm(-2)center dot h(-1/2) from 100 to 310 h, and 11.8 x 10(-2) mg center dot cm(-2)center dot h(-1/2) from 310 to 1098 h. XRD, SEM, and EPMA were used to study the microstructure of the coating. The results indicated that the oxidation took place throughout the entire coating instead of only at the surface. The aluminum phase in the composite coating was soon oxidized to Al2O3 in all tested cases. The aluminum in TiAl3 phase was depleted gradually and oxidized to Al2O3 along with the degradation of TiAl3 to TiAl2 and TiAl as the temperature increased and time proceeded. AlTi2N was also a typical oxidation product at temperature higher than 800 A degrees C. The experimental results also indicated that the protection of the coating was attributed greatly to the interlayer formed between the coating and the substrate.
关键词	cold spray high-temperature oxidation orthorhombic Ti2AlNb alloy TiAl3/Al composite coating
资助者	National Natural Science Foundation of China
DOI	10.1007/s11666-010-9473-4
收录类别	SCI
语种	英语
资助项目	National Natural Science Foundation of China[50971127]
WOS研究方向	Materials Science
WOS类目	Materials Science, Coatings & Films
WOS记录号	WOS:000274904200014
出版者	SPRINGER
引用统计	被引频次：19[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/100479
专题	中国科学院金属研究所
通讯作者	Kong, Lingyan
作者单位	Chinese Acad Sci, State Key Lab Corros & Protect, Inst Met Res, Shenyang 110016, Peoples R China
推荐引用方式 GB/T 7714	Kong, Lingyan,Lu, Bin,Cui, Xinyu,et al. Oxidation Behavior of TiAl3/Al Composite Coating on Orthorhombic-Ti2AlNb Based Alloy at Different Temperatures[J]. JOURNAL OF THERMAL SPRAY TECHNOLOGY,2010,19(3):650-656.
APA	Kong, Lingyan,Lu, Bin,Cui, Xinyu,Du, Hao,Li, Tiefan,&Xiong, Tianying.(2010).Oxidation Behavior of TiAl3/Al Composite Coating on Orthorhombic-Ti2AlNb Based Alloy at Different Temperatures.JOURNAL OF THERMAL SPRAY TECHNOLOGY,19(3),650-656.
MLA	Kong, Lingyan,et al."Oxidation Behavior of TiAl3/Al Composite Coating on Orthorhombic-Ti2AlNb Based Alloy at Different Temperatures".JOURNAL OF THERMAL SPRAY TECHNOLOGY 19.3(2010):650-656.