| SURFACE CRAZING OF Mn-Cu WEATHERING STEEL | |
| Wang Lei1; Zhang Sixun2; Dong Junhua1; Ke Wei1; Liu Chunming2 | |
| 通讯作者 | Dong Junhua(jhdong@imr.ac.cn) |
| 2010-06-11 | |
| 发表期刊 | ACTA METALLURGICA SINICA
 |
| ISSN | 0412-1961 |
| 卷号 | 46期号:6页码:723-728 |
| 摘要 | Craze cracks and oxidation appeared on the surfaces of the Mn-Cu weathering steel samples after different soaking times at 1260 degrees C in the oxidizing conditions. EPMA result shows that Cu enriches at the interface of matrix/scale, Cu concentration in pearlite is higher than that in ferrite. OM observation shows that decarbonization phenomenon occurred near surface of steel after soaking in high temperature experiments, which resulted in an obvious decrease of pearlite amount, so more Cu segregation in grain boundaries and formed Cu-enriched phase, and caused serious surface crazing at last. However, under the reducing condition, the craze crack phenomenon did not occur after soaking. |
| 关键词 | Mn-Cu weathering steel surface crazing soaking decarbonization |
| 资助者 | National Basic Research Program of China ; National Natural Science Foundation of China |
| DOI | 10.3724/SP.J.1037.2009.00501 |
| 收录类别 | SCI |
| 语种 | 英语 |
| 资助项目 | National Basic Research Program of China[2004CB619101] ; National Natural Science Foundation of China[50499336] ; National Natural Science Foundation of China[50971120] |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| WOS类目 | Metallurgy & Metallurgical Engineering |
| WOS记录号 | WOS:000280030800012 |
| 出版者 | SCIENCE CHINA PRESS |
| 引用统计 | |
| 文献类型 | 期刊论文 |
| 条目标识符 | http://ir.imr.ac.cn/handle/321006/100788 |
| 专题 | 中国科学院金属研究所 |
| 通讯作者 | Dong Junhua |
| 作者单位 | 1.Chinese Acad Sci, State Key Lab Corros & Protect, Inst Met Res, Shenyang 110016, Peoples R China 2.Northeast Univ, Inst Mat & Met, Shenyang 110819, Peoples R China |
| 推荐引用方式 GB/T 7714 | Wang Lei,Zhang Sixun,Dong Junhua,et al. SURFACE CRAZING OF Mn-Cu WEATHERING STEEL[J]. ACTA METALLURGICA SINICA,2010,46(6):723-728. |
| APA | Wang Lei,Zhang Sixun,Dong Junhua,Ke Wei,&Liu Chunming.(2010).SURFACE CRAZING OF Mn-Cu WEATHERING STEEL.ACTA METALLURGICA SINICA,46(6),723-728. |
| MLA | Wang Lei,et al."SURFACE CRAZING OF Mn-Cu WEATHERING STEEL".ACTA METALLURGICA SINICA 46.6(2010):723-728. |
| 条目包含的文件 | 条目无相关文件。 | |||||
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论