Microstructural evolution of a directionally solidified nickel-base superalloy during thermal fatigue | |
Xia Pengcheng1,2; Yang Lei1; Yu Jinjiang2; Sun Xiaofeng2; Guan Hengrong2; Hu Zhuangqi2 | |
Corresponding Author | Xia Pengcheng(xpc328@126.com) |
2011-03-01 | |
Source Publication | RARE METALS
![]() |
ISSN | 1001-0521 |
Volume | 30Pages:477-481 |
Abstract | The transition of gamma' phase and dislocation during thermal fatigue test was investigated. There is gamma' denuded region in two sides and the tip of thermal fatigue crack because of oxidation during thermal fatigue test. gamma' phase coarsens and rafts. The direction of gamma' rafting is perpendicular to the orientation of crystal growth. High density dislocations are found near crack. Single dislocation moves in the matrix apart from crack. A few dislocations shear gamma' phase because of relatively low strength of gamma' phase at high temperature. |
Keyword | nickel-base superalloy thermal fatigue gamma ' rafting dislocations |
Funding Organization | National Basic Research Program (973 Program) of China ; National Natural Science Foundation of China (NSFC) |
DOI | 10.1007/s12598-011-0328-z |
Indexed By | SCI |
Language | 英语 |
Funding Project | National Basic Research Program (973 Program) of China[2010CB631200 (2010CB631206)] ; National Natural Science Foundation of China (NSFC)[50931004] |
WOS Research Area | Materials Science ; Metallurgy & Metallurgical Engineering |
WOS Subject | Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
WOS ID | WOS:000303126300102 |
Publisher | NONFERROUS METALS SOC CHINA |
Citation statistics | |
Document Type | 期刊论文 |
Identifier | http://ir.imr.ac.cn/handle/321006/105419 |
Collection | 中国科学院金属研究所 |
Corresponding Author | Xia Pengcheng |
Affiliation | 1.Shandong Univ Sci & Technol, Sch Mat Sci & Engn, Qingdao 266510, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China |
Recommended Citation GB/T 7714 | Xia Pengcheng,Yang Lei,Yu Jinjiang,et al. Microstructural evolution of a directionally solidified nickel-base superalloy during thermal fatigue[J]. RARE METALS,2011,30:477-481. |
APA | Xia Pengcheng,Yang Lei,Yu Jinjiang,Sun Xiaofeng,Guan Hengrong,&Hu Zhuangqi.(2011).Microstructural evolution of a directionally solidified nickel-base superalloy during thermal fatigue.RARE METALS,30,477-481. |
MLA | Xia Pengcheng,et al."Microstructural evolution of a directionally solidified nickel-base superalloy during thermal fatigue".RARE METALS 30(2011):477-481. |
Files in This Item: | There are no files associated with this item. |
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment