Effect of polarization on crack initiation and dislocation behaviour near the surface of A537 steel during low cycle corrosion fatigue in 3.5% NaCl solution
Wang, JQ; Li, J; Ke, W
通讯作者Wang, JQ()
1998-02-15
发表期刊JOURNAL OF MATERIALS SCIENCE LETTERS
ISSN0261-8028
卷号17期号:4页码:345-348
收录类别SCI
语种英语
WOS研究方向Materials Science
WOS类目Materials Science, Multidisciplinary
WOS记录号WOS:000072084800024
出版者KLUWER ACADEMIC PUBL
引用统计
被引频次:2[WOS]   [WOS记录]     [WOS相关记录]
文献类型期刊论文
条目标识符http://ir.imr.ac.cn/handle/321006/108243
专题中国科学院金属研究所
通讯作者Wang, JQ
作者单位Acad Sinica, Inst Corros & Protect Met, Corros Sci Lab, Shenyang 110015, Peoples R China
推荐引用方式
GB/T 7714
Wang, JQ,Li, J,Ke, W. Effect of polarization on crack initiation and dislocation behaviour near the surface of A537 steel during low cycle corrosion fatigue in 3.5% NaCl solution[J]. JOURNAL OF MATERIALS SCIENCE LETTERS,1998,17(4):345-348.
APA Wang, JQ,Li, J,&Ke, W.(1998).Effect of polarization on crack initiation and dislocation behaviour near the surface of A537 steel during low cycle corrosion fatigue in 3.5% NaCl solution.JOURNAL OF MATERIALS SCIENCE LETTERS,17(4),345-348.
MLA Wang, JQ,et al."Effect of polarization on crack initiation and dislocation behaviour near the surface of A537 steel during low cycle corrosion fatigue in 3.5% NaCl solution".JOURNAL OF MATERIALS SCIENCE LETTERS 17.4(1998):345-348.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Wang, JQ]的文章
[Li, J]的文章
[Ke, W]的文章
百度学术
百度学术中相似的文章
[Wang, JQ]的文章
[Li, J]的文章
[Ke, W]的文章
必应学术
必应学术中相似的文章
[Wang, JQ]的文章
[Li, J]的文章
[Ke, W]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。