Microstructure, interface and mechanical property of the DS NiAl/Cr(Mo,Hf) composite
Guo, JT; Cui, CY; Chen, YX; Li, DX; Ye, HQ
Corresponding AuthorGuo, JT()
2001-04-01
Source PublicationINTERMETALLICS
ISSN0966-9795
Volume9Issue:4Pages:287-297
AbstractA NiAl-Cr(Mo) composite containing Hf was directionally solidified under Ar atmosphere in Al2O3-SiO2 ceramic mold by the standard Bridgman method. The microstructure in the as-grown and hot isostatic pressing (HIP) conditions was studied using SEM, HREM and TEM equipped with EDXS. The composite was mainly composed of three phases, i.e. lamellar Cr(Mo), NiAl matrix and semi-continuously distributed Ni2AlHf. The common growth direction of NiAl and Cr(Mo) is < 111 >, and the interface between them was atomically flat with no transition layer. Fine G-phase precipitates were formed in the presence of Si which was from the ceramic shell molds used during the directional solidification. The G-phase precipitates were cuboidal in shape and coherent with NiAl matrix. After the HIPed and aged treatment, the G-phase precipitates completely disappeared and the amount of intercellular Ni2AlHf phase was partially reduced. The mechanical properties were measured by tensile and compressive tests within the temperature range of 25 similar to 1100 degreesC. The BDTT of the HIPed and aged materials is significantly higher than the as-grown composite. The yield stress of the composite was higher than that of many NiAl-based alloys and possible strengthening mechanism were discussed. (C) 2001 Elsevier Science Ltd. All rights reserved.
Keywordnickel aluminides based on NiAl brittleness and ductility mechanical properties at high temperatures hot isostatic dressing microstructure
Indexed BySCI
Language英语
WOS Research AreaChemistry ; Materials Science ; Metallurgy & Metallurgical Engineering
WOS SubjectChemistry, Physical ; Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS IDWOS:000168566700004
PublisherELSEVIER SCI LTD
Citation statistics
Cited Times:78[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/111851
Collection中国科学院金属研究所
Corresponding AuthorGuo, JT
AffiliationChinese Acad Sci, Met Res Inst, Shenyang 110016, Peoples R China
Recommended Citation
GB/T 7714
Guo, JT,Cui, CY,Chen, YX,et al. Microstructure, interface and mechanical property of the DS NiAl/Cr(Mo,Hf) composite[J]. INTERMETALLICS,2001,9(4):287-297.
APA Guo, JT,Cui, CY,Chen, YX,Li, DX,&Ye, HQ.(2001).Microstructure, interface and mechanical property of the DS NiAl/Cr(Mo,Hf) composite.INTERMETALLICS,9(4),287-297.
MLA Guo, JT,et al."Microstructure, interface and mechanical property of the DS NiAl/Cr(Mo,Hf) composite".INTERMETALLICS 9.4(2001):287-297.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Guo, JT]'s Articles
[Cui, CY]'s Articles
[Chen, YX]'s Articles
Baidu academic
Similar articles in Baidu academic
[Guo, JT]'s Articles
[Cui, CY]'s Articles
[Chen, YX]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Guo, JT]'s Articles
[Cui, CY]'s Articles
[Chen, YX]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.