Oxidation behaviour of beta-FeAlCr coating produced by close-field unbalanced magnetron sputter deposition | |
Liu, Z; Gao, W; Wang, F | |
Corresponding Author | Liu, Z() |
2001 | |
Source Publication | HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 5, PTS 1 AND 2
![]() |
ISSN | 0255-5476 |
Volume | 369-3Pages:295-302 |
Abstract | beta -FeAl coatings containing 5.7at.% Cr were produced with a close-field unbalanced magnetron sputter (CFUMS) deposition technique. Cyclic oxidation test at 1100 degreesC in air for 100 1-h cycles and isothermal exposures from 1000 degreesC through 1200 degreesC in pure O-2 for 100 hours were carried out with the coatings. The coating showed better scale spallation resistance during cyclic oxidation test than the cast FeAl. After the isothermal oxidation at 1000 degreesC and 1100 degreesC, fine-grained ridge-type oxide scales were formed on the coatings, while at 1000 degreesC, the oxide scale formed on the cast FeAl showed a large quantity of theta -Al2O3 blades, and big interfacial voids on the base alloy surface were observed. The transformation from theta to alpha -Al2O3 was accelerated due to the presence of Cr in the coatings, and suppressed the fast outward Al diffusion for the growth of theta -Al2O3 scale and eliminated the formation of interfacial voids that deteriorated the oxide scale spallation resistance. After the isothermal exposure at 1200 degreesC, however, the oxide scale on the coating was greatly buckled and spalled, and did not show much improvement over the cast FeAl. |
Keyword | CFUMS oxidation ridge-type oxide beta-FeAlCr coatings theta ->alpha-Al2O3 transformation |
Indexed By | SCI |
Language | 英语 |
WOS Research Area | Materials Science |
WOS Subject | Materials Science, Ceramics ; Materials Science, Multidisciplinary ; Materials Science, Coatings & Films |
WOS ID | WOS:000172513200031 |
Publisher | TRANS TECH PUBLICATIONS LTD |
Citation statistics | |
Document Type | 期刊论文 |
Identifier | http://ir.imr.ac.cn/handle/321006/113290 |
Collection | 中国科学院金属研究所 |
Corresponding Author | Liu, Z |
Affiliation | 1.Univ Auckland, Dept Chem & Mat Engn, Auckland, New Zealand 2.Acad Sinica, Inst Met Res, State Key Lab Corros & Protect, Shenyang 110015, Peoples R China |
Recommended Citation GB/T 7714 | Liu, Z,Gao, W,Wang, F. Oxidation behaviour of beta-FeAlCr coating produced by close-field unbalanced magnetron sputter deposition[J]. HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 5, PTS 1 AND 2,2001,369-3:295-302. |
APA | Liu, Z,Gao, W,&Wang, F.(2001).Oxidation behaviour of beta-FeAlCr coating produced by close-field unbalanced magnetron sputter deposition.HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 5, PTS 1 AND 2,369-3,295-302. |
MLA | Liu, Z,et al."Oxidation behaviour of beta-FeAlCr coating produced by close-field unbalanced magnetron sputter deposition".HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 5, PTS 1 AND 2 369-3(2001):295-302. |
Files in This Item: | There are no files associated with this item. |
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment