Anisotropy of high temperature stress rupture property of a Ni base single crystal superalloy
Liu, JL; Jin, T; Zhang, JH; Hu, ZQ
Corresponding AuthorLiu, JL(jlliu@imr.ac.cn)
2001-12-18
Source PublicationACTA METALLURGICA SINICA
ISSN0412-1961
Volume37Issue:12Pages:1233-1237
AbstractThe stress rupture test was conducted to a Ni base single crystal superalloy along [001],[011] and [111] orientations. The results show that the [001] oriented specimen has the best ductility and the [111] oriented specimen has the longest lifetime ,while the [011] oriented specimen is lower at these two properties. The longest lifetime in [111] orientation is resulting from the formation of dislocation networks due to multislip and its lower resolved shear stress. The [001] orientation specimen displays the best ductility owing to the blunting effect to microcrack stemming from multiple equivalent slip systems. The [011] oriented specimen has lower lifetime and bad ductility because of its higher resolved stress and less slip systems, even the deformation twinning also promotes the initiation of crack. A vine-like gamma' is formed along dendrite direction in all three orientations during test, which is caused by the small misorietation between dendrites and this vine-like gamma' can act as an important crack initiation site.
KeywordNi base single crystal superalloy stress rupture property anisotropy
Indexed BySCI
Language英语
WOS Research AreaMetallurgy & Metallurgical Engineering
WOS SubjectMetallurgy & Metallurgical Engineering
WOS IDWOS:000173281800001
PublisherSCIENCE CHINA PRESS
Citation statistics
Cited Times:19[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/113484
Collection中国科学院金属研究所
Corresponding AuthorLiu, JL
AffiliationChinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China
Recommended Citation
GB/T 7714
Liu, JL,Jin, T,Zhang, JH,et al. Anisotropy of high temperature stress rupture property of a Ni base single crystal superalloy[J]. ACTA METALLURGICA SINICA,2001,37(12):1233-1237.
APA Liu, JL,Jin, T,Zhang, JH,&Hu, ZQ.(2001).Anisotropy of high temperature stress rupture property of a Ni base single crystal superalloy.ACTA METALLURGICA SINICA,37(12),1233-1237.
MLA Liu, JL,et al."Anisotropy of high temperature stress rupture property of a Ni base single crystal superalloy".ACTA METALLURGICA SINICA 37.12(2001):1233-1237.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Liu, JL]'s Articles
[Jin, T]'s Articles
[Zhang, JH]'s Articles
Baidu academic
Similar articles in Baidu academic
[Liu, JL]'s Articles
[Jin, T]'s Articles
[Zhang, JH]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Liu, JL]'s Articles
[Jin, T]'s Articles
[Zhang, JH]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.