Tribological behaviors of superalloy IC-6 and its protective coating
Wang, B; Gong, J; Wang, AY; Sun, C; Huang, RF; Wen, LS
Corresponding AuthorWang, B()
2002-07-01
Source PublicationACTA METALLURGICA SINICA
ISSN0412-1961
Volume38Issue:7Pages:750-754
AbstractNiCrAlY coatings were deposited on superalloy IC-6 by arc ion plating (AIP). Unlubricated friction and wear behaviors of NiCrAlY coated alloy IC-6 and uncoated alloy IC-6 against alloy K17 were studied. The results indicate that in wear performance at room temperature, debris came off from alloy K17 and then transferred to the surface of alloy IC-6. Both alloy IC-6 and NiCrAly coating could be oxidized after 6000 cycles. However, oxygen is not in high concentration because only a small amount of stable oxides form in such a short time even the temperature on contact surface reached 300 V. During wear process at 600 degreesC, oxides could form more rapidly on the surface of NiCrAlY coating and impeded the interaction between substrate alloys. Oxides became more viscoidal with the temperature increment on the contact surface. Therefore, the friction coefficients is higher at room temperature than at 600 degreesC.
Keywordtribological behavior superalloy NiCrAlY coating arc ion plating
Indexed BySCI
Language英语
WOS Research AreaMetallurgy & Metallurgical Engineering
WOS SubjectMetallurgy & Metallurgical Engineering
WOS IDWOS:000177354700017
PublisherSCIENCE CHINA PRESS
Citation statistics
Cited Times:2[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/114941
Collection中国科学院金属研究所
Corresponding AuthorWang, B
AffiliationChinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China
Recommended Citation
GB/T 7714
Wang, B,Gong, J,Wang, AY,et al. Tribological behaviors of superalloy IC-6 and its protective coating[J]. ACTA METALLURGICA SINICA,2002,38(7):750-754.
APA Wang, B,Gong, J,Wang, AY,Sun, C,Huang, RF,&Wen, LS.(2002).Tribological behaviors of superalloy IC-6 and its protective coating.ACTA METALLURGICA SINICA,38(7),750-754.
MLA Wang, B,et al."Tribological behaviors of superalloy IC-6 and its protective coating".ACTA METALLURGICA SINICA 38.7(2002):750-754.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Wang, B]'s Articles
[Gong, J]'s Articles
[Wang, AY]'s Articles
Baidu academic
Similar articles in Baidu academic
[Wang, B]'s Articles
[Gong, J]'s Articles
[Wang, AY]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Wang, B]'s Articles
[Gong, J]'s Articles
[Wang, AY]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.