Formation of the high chromium white iron parts with gradient structure via semisolid metal extrusion

IMR OpenIR

	Formation of the high chromium white iron parts with gradient structure via semisolid metal extrusion
	Yang, Z; Zhang, HF; Wang, AM; Ding, BZ; Hu, ZG
通讯作者	Zhang, HF()
	2003-02-11
发表期刊	ACTA METALLURGICA SINICA
ISSN	0412-1961
卷号	39 期号:2 页码:164-167
摘要	The high chromium white iron with equiaxed primary structure was extruded at semisolid state. The liquid phase was squeezed out by pressure. After solidification, the volume percentage of the eutectic structure increases gradually from the center to the perimeter. Test shows that the extrusion temperatures have great effect on the structure of the extruded sample. The compact toughness at the center of the sample and the wear resistance at the perimeter of the sample are improved.
关键词	semi-solid metal extrusion high chromium white iron gradient structure
收录类别	SCI
语种	英语
WOS研究方向	Metallurgy & Metallurgical Engineering
WOS类目	Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000181652500011
出版者	SCIENCE CHINA PRESS
引用统计	被引频次：2[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/117307
专题	中国科学院金属研究所
通讯作者	Zhang, HF
作者单位	Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China
推荐引用方式 GB/T 7714	Yang, Z,Zhang, HF,Wang, AM,et al. Formation of the high chromium white iron parts with gradient structure via semisolid metal extrusion[J]. ACTA METALLURGICA SINICA,2003,39(2):164-167.
APA	Yang, Z,Zhang, HF,Wang, AM,Ding, BZ,&Hu, ZG.(2003).Formation of the high chromium white iron parts with gradient structure via semisolid metal extrusion.ACTA METALLURGICA SINICA,39(2),164-167.
MLA	Yang, Z,et al."Formation of the high chromium white iron parts with gradient structure via semisolid metal extrusion".ACTA METALLURGICA SINICA 39.2(2003):164-167.