The effect of nickel aluminide (NiAl) microcrystalline coating prepared by magnetron-sputtering on the high-temperature oxidation behavior of the NiAl-33.5Cr-0.5Zr (at%) alloy was investigated in static air from 1,000degreesC to 1,150degreesC. The additions of Cr and Zr changed the single 0 phase structure into the multiphase structure (beta-NiAl, alpha-Cr. and Heusler [Ni2AlZr] phase). The NiAl-33.5Cr-0.5Zr alloy formed a nonprotective Al2O3 + Cr2O3 + ZrO2 (aluminum oxide + chromium oxide + zirconium dioxide) mixed scale and exhibited relatively large weight gains. The large weight gains were attributed to extensive internal oxidation. The sputtered NiAl microcrystalline coating remarkably improved the oxidation resistance compared to the NiAl-33.5Cr-0.5Zr alloy due to the formation of a continuous Al2O3 scalefrom 1,000degreesC to 1, 150degreesC. The metastable theta-Al2O3 --> alpha-Al2O3 transformation was identified by x-ray diffraction (XRD) results and a change in the morphology of scales also occurred with the transformation.
Chinese Acad Sci, Met Res Inst, Shenyang 110016, Peoples R China
推荐引用方式 GB/T 7714
Xu, CM,Guo, JT. Effect of nickel aluminide microcrystalline coating on high-temperature oxidation behavior of NiAl-33.5%Cr-0.5%Zr alloy[J]. CORROSION,2003,59(4):350-355.
APA
Xu, CM,&Guo, JT.(2003).Effect of nickel aluminide microcrystalline coating on high-temperature oxidation behavior of NiAl-33.5%Cr-0.5%Zr alloy.CORROSION,59(4),350-355.
MLA
Xu, CM,et al."Effect of nickel aluminide microcrystalline coating on high-temperature oxidation behavior of NiAl-33.5%Cr-0.5%Zr alloy".CORROSION 59.4(2003):350-355.
修改评论