Oxidation behaviour of the alloy IC-6 and protective coatings
Wang, B; Sun, C; Gong, J; Huang, RF; Wen, LS
Corresponding AuthorSun, C(
AbstractIn this work, NiCoCrAlY coatings were deposited on a new Ni-base alloy, IC-6. The oxidation kinetic curves of alloy IC-6, K 17 and NiCoCrAlY coatings on alloy IC-6 at 900-1100 degreesC were obtained. The results indicated that the oxide scales consisted of alpha-Al2O3, NiAl2O4, NiO, as well as a small amount of NiMoO4 and MoO2. These scales occurred after alloy IC-6 exposure at 900 degreesC for 100 It. The weight loss occurred when alloy IC-6 were exposed at 1050 and 1100 degreesC due to the formation of volatile MoO3. After the NiCoCrAlY coating was deposited, the scales mainly contained alpha-Al2O3, when the specimens were oxidized at 900 degreesC, and alpha-Al2O3 and Cr2O3 at 1050 degreesC. The formation of alpha-Al2O3 and Cr2O3 scales on NiCoCrAlY coating was directly responsible for improving oxidation resistance of the alloy IC-6. (C) 2003 Elsevier Ltd. All rights reserved.
Keywordsuperalloy NiCoCrAlY coating oxidation arc ion plating
Indexed BySCI
WOS Research AreaMaterials Science ; Metallurgy & Metallurgical Engineering
WOS SubjectMaterials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS IDWOS:000187856800002
Citation statistics
Cited Times:32[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Corresponding AuthorSun, C
Affiliation1.Chinese Acad Sci, Met Res Inst, Dept Surface Engn Mat, Shenyang 110016, Peoples R China
2.Hahn Meitner Inst Berlin GmbH, D-14109 Berlin, Germany
Recommended Citation
GB/T 7714
Wang, B,Sun, C,Gong, J,et al. Oxidation behaviour of the alloy IC-6 and protective coatings[J]. CORROSION SCIENCE,2004,46(3):519-528.
APA Wang, B,Sun, C,Gong, J,Huang, RF,&Wen, LS.(2004).Oxidation behaviour of the alloy IC-6 and protective coatings.CORROSION SCIENCE,46(3),519-528.
MLA Wang, B,et al."Oxidation behaviour of the alloy IC-6 and protective coatings".CORROSION SCIENCE 46.3(2004):519-528.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Wang, B]'s Articles
[Sun, C]'s Articles
[Gong, J]'s Articles
Baidu academic
Similar articles in Baidu academic
[Wang, B]'s Articles
[Sun, C]'s Articles
[Gong, J]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Wang, B]'s Articles
[Sun, C]'s Articles
[Gong, J]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.