Effect of Hydrogen on Cavitation Erosion Behaviour of High Strength Steel

doi:10.20964/2016.12.34

IMR OpenIR

	Effect of Hydrogen on Cavitation Erosion Behaviour of High Strength Steel
	Qiao, Y. X.1; Cai, X.1; Ouyang, C.1; Zheng, Y. G.2
通讯作者	Qiao, Y. X.(yxqiao@imr.ac.cn) ; Ouyang, C.(oyc1014@163.com)
	2016-12-01
发表期刊	INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE
ISSN	1452-3981
卷号	11 期号:12 页码:10329-10346
摘要	The cavitation erosion behaviors of high strength steel electrochemically charged with hydrogen in distilled water and 3.5% NaCl solution were investigated. The results showed the surface hardness of the steel increased by electrochemical hydrogen-charging but no noticeable effect on the E-corr under condition of quiescence and cavitation respectively. Under condition of cavitation the corrosion rate was enhanced, especially for specimen electrochemically charged with hydrogen at 50 mA.cm(-2) for 12 hours. The mass loss increased with the increasing of current density of electrochemical hydrogen charging. The corrosion induced by erosion played an important role in the synergistic effect under condition of cavitation and electrochemistry was confirmed that hydrogen embrittlement had a great influence on cavitation erosion of high strength steel.
关键词	Low alloy steel Erosion Hydrogen embrittlement Hardening
资助者	Startup project of Doctor Scientific Research of Jiangsu University of Science and Technology
DOI	10.20964/2016.12.34
收录类别	SCI
语种	英语
资助项目	Startup project of Doctor Scientific Research of Jiangsu University of Science and Technology[1062921401]
WOS研究方向	Electrochemistry
WOS类目	Electrochemistry
WOS记录号	WOS:000391039000046
出版者	ESG
引用统计	被引频次：5[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/123602
专题	中国科学院金属研究所
通讯作者	Qiao, Y. X.; Ouyang, C.
作者单位	1.Jiangsu Univ Sci & Technol, Zhenjiang 212003, Jiangsu, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China
推荐引用方式 GB/T 7714	Qiao, Y. X.,Cai, X.,Ouyang, C.,et al. Effect of Hydrogen on Cavitation Erosion Behaviour of High Strength Steel[J]. INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE,2016,11(12):10329-10346.
APA	Qiao, Y. X.,Cai, X.,Ouyang, C.,&Zheng, Y. G..(2016).Effect of Hydrogen on Cavitation Erosion Behaviour of High Strength Steel.INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE,11(12),10329-10346.
MLA	Qiao, Y. X.,et al."Effect of Hydrogen on Cavitation Erosion Behaviour of High Strength Steel".INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE 11.12(2016):10329-10346.