Effect of Tungsten Fiber Diameter on Penetration Ability of Zr-based Metallic Glass Composites

IMR OpenIR

	Effect of Tungsten Fiber Diameter on Penetration Ability of Zr-based Metallic Glass Composites
	Du Chengxin 1; Du Zhonghua 1; Zhu Zhengwang 2
通讯作者	Du Chengxin(duchengxin4324@163.com)
	2017-04-01
发表期刊	RARE METAL MATERIALS AND ENGINEERING
ISSN	1002-185X
卷号	46 期号:4 页码:1080-1085
摘要	Penetration experiments were conducted for Zr-based metallic glass composites containing tungsten fibers with different diameters of 0.3, 0.5, 0.7, 1.0 mm to perforate homogeneous armor steel at velocity of (1270 +/- 40) m/s. Meanwhile their characteristics and depths of penetration were compared with those of tungsten alloy. Results demonstrate that under the same preparation condition, the diameter of the tungsten fiber is a critical parameter for penetration ability. Firstly, the curve of the diameter of the tungsten with the penetration depth is convex when it perforates ideally and the composite containing 0.7 mm tungsten fiber obtains the maximum penetration depth of 55 mm which is increased by 25% compared with that of tungsten alloy because the failure mode is adiabatic shear failure during the penetration similar to that of the depleted uranium alloy exhibiting a crater of 90 degrees at bottom. Secondly, the diameter of tungsten fiber influences the failure mode of the head of the composites significantly. With the increasing of the tungsten fiber diameter, the failure mode ranges from a composite failure mode that includes deformation, splitting, bending and crack to adiabatic shear failure and then it turns to composite failure mode again.
关键词	tungsten fiber diameter Zr-based metallic glass composites penetration adiabatic shear
收录类别	SCI
语种	英语
WOS研究方向	Materials Science ; Metallurgy & Metallurgical Engineering
WOS类目	Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000400722000036
出版者	NORTHWEST INST NONFERROUS METAL RESEARCH
引用统计	被引频次：4[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/124241
专题	中国科学院金属研究所
通讯作者	Du Chengxin
作者单位	1.Nanjing Univ Sci & Technol, Nanjing 210094, Jiangsu, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China
推荐引用方式 GB/T 7714	Du Chengxin,Du Zhonghua,Zhu Zhengwang. Effect of Tungsten Fiber Diameter on Penetration Ability of Zr-based Metallic Glass Composites[J]. RARE METAL MATERIALS AND ENGINEERING,2017,46(4):1080-1085.
APA	Du Chengxin,Du Zhonghua,&Zhu Zhengwang.(2017).Effect of Tungsten Fiber Diameter on Penetration Ability of Zr-based Metallic Glass Composites.RARE METAL MATERIALS AND ENGINEERING,46(4),1080-1085.
MLA	Du Chengxin,et al."Effect of Tungsten Fiber Diameter on Penetration Ability of Zr-based Metallic Glass Composites".RARE METAL MATERIALS AND ENGINEERING 46.4(2017):1080-1085.