INHIBITION EFFECTS OF I- AND I2 ON STRESS-CORROSION CRACKING OF STAINLESS-STEEL IN ACIDIC CHLORIDE SOLUTIONS
HUANG, YL; CAO, CN; LU, M; LIN, HC
通讯作者HUANG, YL()
1993-08-01
发表期刊CORROSION
ISSN0010-9312
卷号49期号:8页码:644-649
摘要Stress corrosion cracking (SCC) of AISI 321 (UNS S32100) stainless steel (SS) in 0.5 mol/L sodium chloride (NaCl) + 0.5 mol/L hydrochloric acid (HCI) solution and the inhibition effects of some iodides and iodine (I2) were studied using the slow strain rate technique. Iodides studied were tetramethyl ammonium iodide (TMAI), tetrabutyl ammonium iodide (TBAI) and potassium iodide (KI). The additives effectively inhibited SCC of AISI 321 in the solution. Inhibition effects resulted mainly from the role of iodide ion. Electrochemical measurements showed the corrosion current density (I(corr)) of the steel increased rapidly and then fluctuated as strain increased. The increase in I(corr) was markedly slower in solutions containing I- ions or I2. Inhibition effects of I- ions and I2 on SCC were attributed to the anodic reaction of the corrosion process and reduction of the accelerating effect of strain on I(corr).
关键词CHLORIDE INHIBITOR STAINLESS STEEL STRESS CORROSION CRACKING
收录类别SCI
语种英语
WOS研究方向Materials Science ; Metallurgy & Metallurgical Engineering
WOS类目Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS记录号WOS:A1993LU76700004
出版者NATL ASSN CORROSION ENG
引用统计
被引频次:17[WOS]   [WOS记录]     [WOS相关记录]
文献类型期刊论文
条目标识符http://ir.imr.ac.cn/handle/321006/125999
专题中国科学院金属研究所
通讯作者HUANG, YL
作者单位CHINESE ACAD SCI,INST CORROS & PROTECT MET,CORROS SCI LAB,SHENYANG 110015,PEOPLES R CHINA
推荐引用方式
GB/T 7714
HUANG, YL,CAO, CN,LU, M,et al. INHIBITION EFFECTS OF I- AND I2 ON STRESS-CORROSION CRACKING OF STAINLESS-STEEL IN ACIDIC CHLORIDE SOLUTIONS[J]. CORROSION,1993,49(8):644-649.
APA HUANG, YL,CAO, CN,LU, M,&LIN, HC.(1993).INHIBITION EFFECTS OF I- AND I2 ON STRESS-CORROSION CRACKING OF STAINLESS-STEEL IN ACIDIC CHLORIDE SOLUTIONS.CORROSION,49(8),644-649.
MLA HUANG, YL,et al."INHIBITION EFFECTS OF I- AND I2 ON STRESS-CORROSION CRACKING OF STAINLESS-STEEL IN ACIDIC CHLORIDE SOLUTIONS".CORROSION 49.8(1993):644-649.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[HUANG, YL]的文章
[CAO, CN]的文章
[LU, M]的文章
百度学术
百度学术中相似的文章
[HUANG, YL]的文章
[CAO, CN]的文章
[LU, M]的文章
必应学术
必应学术中相似的文章
[HUANG, YL]的文章
[CAO, CN]的文章
[LU, M]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。