Effect of small amount of nitrogen on carbide characteristics in unidirectional Ni-base superalloy
Huang, XB; Zhang, Y; Liu, YL; Hu, ZQ
通讯作者Huang, XB()
1997-10-01
发表期刊METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE
ISSN1073-5623
卷号28期号:10页码:2143-2147
摘要The shape, size, and content of MC carbides in a unidirectional Ni-base superalloy have been studied at different solidification rates using material of normal commercial composition (5 ppm nitrogen) and two melts with additions to produce 22 and 30 ppm nitrogen. M(C,N) was found in nitrogen-doped specimens. The increased nitrogen content results in a change in carbide morphology from acicular or Chinese-script type to a blocky one. Carbide size increases from 6.85 to 7.25 mu m at 2.5 mu m/s and from 2.31 to 2.81 mu m at 200 mu m/s as the nitrogen content increases from 5 to 22 ppm; carbide size is reduced to 5.2 mu m at 2.5 mu m/s and to 2.1 mu m at 200 mu m/s when nitrogen content is further raised to 30 ppm. There is no evident change in carbide content (area percentage) with increase of nitrogen. Scanning electron microscopy (SEM) and electron probe microanalysis revealed characteristic centers in some of the blocky carbides of TiN, as nuclei of MC or M(C,N) formed in the melt. The influences of nitrogen on carbide at the low solidification rate are stronger than those at the higher rate. With the increase of solidification rate, the carbide turns from bar to Chinese-script type, except for the base alloy at 2.5 mu m/s, and the content and size decrease.
收录类别SCI
语种英语
WOS研究方向Materials Science ; Metallurgy & Metallurgical Engineering
WOS类目Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS记录号WOS:A1997YA65600020
出版者MINERALS METALS MATERIALS SOC
引用统计
被引频次:49[WOS]   [WOS记录]     [WOS相关记录]
文献类型期刊论文
条目标识符http://ir.imr.ac.cn/handle/321006/126809
专题中国科学院金属研究所
通讯作者Huang, XB
作者单位CHINESE ACAD SCI,MET RES INST,SHENYANG 110015,PEOPLES R CHINA
推荐引用方式
GB/T 7714
Huang, XB,Zhang, Y,Liu, YL,et al. Effect of small amount of nitrogen on carbide characteristics in unidirectional Ni-base superalloy[J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE,1997,28(10):2143-2147.
APA Huang, XB,Zhang, Y,Liu, YL,&Hu, ZQ.(1997).Effect of small amount of nitrogen on carbide characteristics in unidirectional Ni-base superalloy.METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE,28(10),2143-2147.
MLA Huang, XB,et al."Effect of small amount of nitrogen on carbide characteristics in unidirectional Ni-base superalloy".METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE 28.10(1997):2143-2147.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Huang, XB]的文章
[Zhang, Y]的文章
[Liu, YL]的文章
百度学术
百度学术中相似的文章
[Huang, XB]的文章
[Zhang, Y]的文章
[Liu, YL]的文章
必应学术
必应学术中相似的文章
[Huang, XB]的文章
[Zhang, Y]的文章
[Liu, YL]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。