Microstructures of Nickel-base Single-Crystal Superalloy Prepared by Laser Solid Forming
Liang Jingjing; Yang Yanhong; Zhou Yizhou; Li Jinguo; Wang Liang; Jin Tao; Sun Xiaofeng
Corresponding AuthorLiang Jingjing(jjliang@imr.ac.cn)
2017-12-01
Source PublicationRARE METAL MATERIALS AND ENGINEERING
ISSN1002-185X
Volume46Issue:12Pages:3753-3759
AbstractSingle-crystal superalloys have been commonly used in modern advanced aero engines to produce high-pressure high-temperature turbine blades. In order to extend the lifetime of single-crystal turbine blades, repair of cracked and worn ones is of great interest. Laser Solid Forming (LSF) is a prospective technology that can be used to repair single-crystal blades. In this study, the microstructure of the as-deposited and heat-treated LSF single-crystal superalloy has been characterized through optical microscopy (OM), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The as-deposited LSF sample shows a directionally solidified columnar dendrites growing almost parallel to the building direction. Between the dendrites, nearly round microporosity and blocky MC carbide particles are dispersed uniformly. TEM results indicate that many nano gamma' particles precipitate in gamma matrix. In addition, during LSF deposition process, stress is formed, which generates plenty of dislocations. During heat treatment, the LSF sample experiences full recrystallization. The recrystallization grains are in different sizes, and twins are found in some recrystallized grains. Because the residual stress is fully released during heat treatment, the size and shape of gamma' precipitates in the recrystallized and un-recrystallized regions are similar to those in conventionally cast samples.
Keywordlaser solid forming single crystal superalloy heat treatment recrystallization
Indexed BySCI
Language英语
WOS Research AreaMaterials Science ; Metallurgy & Metallurgical Engineering
WOS SubjectMaterials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS IDWOS:000425203200028
PublisherNORTHWEST INST NONFERROUS METAL RESEARCH
Citation statistics
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/127396
Collection中国科学院金属研究所
Corresponding AuthorLiang Jingjing
AffiliationChinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China
Recommended Citation
GB/T 7714
Liang Jingjing,Yang Yanhong,Zhou Yizhou,et al. Microstructures of Nickel-base Single-Crystal Superalloy Prepared by Laser Solid Forming[J]. RARE METAL MATERIALS AND ENGINEERING,2017,46(12):3753-3759.
APA Liang Jingjing.,Yang Yanhong.,Zhou Yizhou.,Li Jinguo.,Wang Liang.,...&Sun Xiaofeng.(2017).Microstructures of Nickel-base Single-Crystal Superalloy Prepared by Laser Solid Forming.RARE METAL MATERIALS AND ENGINEERING,46(12),3753-3759.
MLA Liang Jingjing,et al."Microstructures of Nickel-base Single-Crystal Superalloy Prepared by Laser Solid Forming".RARE METAL MATERIALS AND ENGINEERING 46.12(2017):3753-3759.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Liang Jingjing]'s Articles
[Yang Yanhong]'s Articles
[Zhou Yizhou]'s Articles
Baidu academic
Similar articles in Baidu academic
[Liang Jingjing]'s Articles
[Yang Yanhong]'s Articles
[Zhou Yizhou]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Liang Jingjing]'s Articles
[Yang Yanhong]'s Articles
[Zhou Yizhou]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.