Preparation and Enhanced Hot Corrosion Resistance of a Zr-Doped PtAl2+(Ni, Pt)Al Dual-Phase Coating

doi:10.11900/0412.1961.2017.00376

IMR OpenIR

	Preparation and Enhanced Hot Corrosion Resistance of a Zr-Doped PtAl2+(Ni, Pt)Al Dual-Phase Coating
	Jiang Chengyang 1,2; Yang Yingfei 2; Zhang Zhengyi 3; Bao Zebin 2; Zhu Shenglong 2; Wang Fuhui 1
通讯作者	Bao Zebin(zbbao@imr.ac.cn)
	2018-04-01
发表期刊	ACTA METALLURGICA SINICA
ISSN	0412-1961
卷号	54 期号:4 页码:581-590
摘要	Prior to practical service, hot-section components (e.g. airfoils and vanes) of a gas turbine engine are necessarily coated by a protective metallic coating (such as aluminidi diffusion coating, modified aluminide coating and MCrAlY overlay etc.) to resist high temperature oxidation and hot corrosion. Among the modified aluminide coatings, the coating with Pt-modification has attracted great attention and is widely used in applications requiring high reliability and extended service life since it possesses superior oxidation/corrosion resistance at high temperature. The presence of Pt in aluminide coating is favorable for increasing bonding strength of oxide scale, enlarging phase region of beta 3-NiAI and confining detrimental effect of sulphur etc. Although Pt-modification has exhibited visible benefits for acquiring better high-temperature performance, it is far from satisfaction to develop an ideal aluminide diffusion coating. Reactive elements such as Y, Hf, Zr or their oxides have been employed to modify the nickel aluminide coating system, with an aim to further improve scale adhesion and promote exclusive formation of alpha-Al2O3 simultaneously. In this work, a Zr-doped PtAl2+(Ni, Pt)Al dual-phase aluminide coating was prepared on a Ni-based single crystal superalloy by co-deposition of Pt-Zr through electroplating and sub-sequent aluminization treatments The coating was mainly composed of three layers: the outmost layer consisted of double phases with PtAl2 particles dispersed in beta-(Ni, Pt)Al domain, while the interlayer comprised beta-(Ni, Pt)Al with small amount of Cr-precipitates, and the bottom layer was an inter-diffusion zone (IDZ). Zirconium was mainly distributed inside beta-(Ni, Pt)Al solid solution in both the outmost layer and the interlayer. Compared with normal PtAl2+(Ni, Pt)Al dual-phase coating, the hot corrosion behavior of the Zr-doped PtAl2 + (Ni, Pt)Al coating was assessed in a salt mixture of Na2SO4/NaCI (75:25, mass ratio) at 850 degrees C in static air. The results indicated that the Zr-doped PtAl2+(Ni, Pt)Al dual-phase coating exhibited superior hot corrosion resistance since Zr was confirmed able to capture and fix S and CI to diminish their detrimental effects. Meanwhile, a pre-oxidation treatment did not effectively improve the overall hot corrosion resistance of normal PtAl2+(Ni, Pt)Al coating because the thin alumina scale formed during pre-oxidation was unable to prohibit the sustained inward-invasion of the mixed salt.
关键词	Zr-doping reactive element Pt-Al coating hot corrosion
资助者	National Natural Science Foundation of China ; Defense Industrial Technology Development Program ; Liaoning BaiQianWan Talents Program
DOI	10.11900/0412.1961.2017.00376
收录类别	SCI
语种	英语
资助项目	National Natural Science Foundation of China[51671202] ; National Natural Science Foundation of China[51301184] ; Defense Industrial Technology Development Program[JCKY2016404C001] ; Liaoning BaiQianWan Talents Program
WOS研究方向	Metallurgy & Metallurgical Engineering
WOS类目	Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000433006500012
出版者	SCIENCE PRESS
引用统计	被引频次：5[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/128535
专题	中国科学院金属研究所
通讯作者	Bao Zebin
作者单位	1.Northeastern Univ, Sch Mat Sci & Engn, Shenyang 110819, Liaoning, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Liaoning, Peoples R China 3.China Natl South Aviat Ind Co Ltd, Zhuzhou 412002, Peoples R China
推荐引用方式 GB/T 7714	Jiang Chengyang,Yang Yingfei,Zhang Zhengyi,et al. Preparation and Enhanced Hot Corrosion Resistance of a Zr-Doped PtAl2+(Ni, Pt)Al Dual-Phase Coating[J]. ACTA METALLURGICA SINICA,2018,54(4):581-590.
APA	Jiang Chengyang,Yang Yingfei,Zhang Zhengyi,Bao Zebin,Zhu Shenglong,&Wang Fuhui.(2018).Preparation and Enhanced Hot Corrosion Resistance of a Zr-Doped PtAl2+(Ni, Pt)Al Dual-Phase Coating.ACTA METALLURGICA SINICA,54(4),581-590.
MLA	Jiang Chengyang,et al."Preparation and Enhanced Hot Corrosion Resistance of a Zr-Doped PtAl2+(Ni, Pt)Al Dual-Phase Coating".ACTA METALLURGICA SINICA 54.4(2018):581-590.