Influence of phase dissolution and hydrogen absorption on the stress corrosion cracking behavior of Mg-7%Gd-5%Y-1%Nd-0.5%Zr alloy in 3.5 wt.% NaCl solution

doi:10.1016/j.corsci.2018.07.019

IMR OpenIR

	Influence of phase dissolution and hydrogen absorption on the stress corrosion cracking behavior of Mg-7%Gd-5%Y-1%Nd-0.5%Zr alloy in 3.5 wt.% NaCl solution
	Wang, S. D.1,2,3; Xu, D. K.1; Wang, B. J.4; Sheng, L. Y.5; Qiao, Y. X.6; Han, En-Hou 1; Dong, C.3
通讯作者	Xu, D. K.(dkxu@imr.ac.cn)
	2018-09-01
发表期刊	CORROSION SCIENCE
ISSN	0010-938X
卷号	142 页码:185-200
摘要	Through investigating the influence of phase dissolution and hydrogen on the stress corrosion cracking (SCC) behavior of an as-cast Mg-7%Gd-5%Y-1%Nd-0.5%Zr alloy in 3.5 wt.% NaCl solution, it revealed that the proposed T4 treatment can improve the SCC resistance. Based on the microstructural analysis, such improvement was mainly ascribed to the complete dissolution of coarse eutectic pockets. Further analysis indicated that the SCC mechanism was associated with hydrogen embrittlement (HE). Through dissolving the eutectic pockets and alleviating the corrosion attack of Mg matrix, the influence of HE on SCC resistance of T4 samples can be weakened.
关键词	Magnesium EIS Stress corrosion Hydrogen embrittlement
资助者	National Key Research and Development Program of China ; National Natural Science Foundation of China ; Strategic New Industry Development Special Foundation of Shenzhen ; Innovation Fund of Institute of Metal Research (IMR), Chinese Academy of Sciences (CAS)
DOI	10.1016/j.corsci.2018.07.019
收录类别	SCI
语种	英语
资助项目	National Key Research and Development Program of China[2017YFB0702001] ; National Key Research and Development Program of China[2016YFB0301105] ; National Natural Science Foundation of China[51701129] ; National Natural Science Foundation of China[51271183] ; National Natural Science Foundation of China[51301172] ; Strategic New Industry Development Special Foundation of Shenzhen[JCYJ20170306141749970] ; Innovation Fund of Institute of Metal Research (IMR), Chinese Academy of Sciences (CAS)
WOS研究方向	Materials Science ; Metallurgy & Metallurgical Engineering
WOS类目	Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000444933400018
出版者	PERGAMON-ELSEVIER SCIENCE LTD
引用统计	被引频次：45[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/129551
专题	中国科学院金属研究所
通讯作者	Xu, D. K.
作者单位	1.Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, 62 Wencui Rd, Shenyang 110016, Peoples R China 2.Univ Alberta, Dept Chem & Mat Engn, Edmonton, AB T6G 1H9, Canada 3.Dalian Univ Technol, Lab Mat Modificat Laser Electron & Ion Beams, Sch Mat Sci & Engn, Dalian 116024, Peoples R China 4.Shenyang Ligong Univ, Sch Environm & Chem Engn, Shenyang 110159, Liaoning, Peoples R China 5.Peking Univ, Shenzhen Inst, Shenzhen Key Lab Human Tissue Regenerate & Repair, Shenzhen 518057, Peoples R China 6.Jiangsu Univ Sci & Technol, Zhenjiang 212003, Peoples R China
推荐引用方式 GB/T 7714	Wang, S. D.,Xu, D. K.,Wang, B. J.,et al. Influence of phase dissolution and hydrogen absorption on the stress corrosion cracking behavior of Mg-7%Gd-5%Y-1%Nd-0.5%Zr alloy in 3.5 wt.% NaCl solution[J]. CORROSION SCIENCE,2018,142:185-200.
APA	Wang, S. D..,Xu, D. K..,Wang, B. J..,Sheng, L. Y..,Qiao, Y. X..,...&Dong, C..(2018).Influence of phase dissolution and hydrogen absorption on the stress corrosion cracking behavior of Mg-7%Gd-5%Y-1%Nd-0.5%Zr alloy in 3.5 wt.% NaCl solution.CORROSION SCIENCE,142,185-200.
MLA	Wang, S. D.,et al."Influence of phase dissolution and hydrogen absorption on the stress corrosion cracking behavior of Mg-7%Gd-5%Y-1%Nd-0.5%Zr alloy in 3.5 wt.% NaCl solution".CORROSION SCIENCE 142(2018):185-200.