Production of alumina micro abrasives coated with nano-silica for bonding improvements to zirconia

doi:10.1080/17458080.2018.1502478

IMR OpenIR

	Production of alumina micro abrasives coated with nano-silica for bonding improvements to zirconia
	Zhang Wei 1,2; Farooq, Ahmad 3; Wu Wangping 1,2; Kong Dejun 1,2
通讯作者	Zhang Wei(zwzy666@cczu.edu.cn)
	2018
发表期刊	JOURNAL OF EXPERIMENTAL NANOSCIENCE
ISSN	1745-8080
卷号	13 期号:1 页码:211-219
摘要	Tribochemical silica coating is a common practice to achieve suitable adhesion with intended synthetic substrates or natural tissues, and the key to this technology is the preparation of alumina abrasive coated by nano-silica (AACNS). In this paper, a novel physical method of producing silicon nanoparticles (SiNPs) that is the base to AACNS is put forward in this paper. The source of the silica coating is from SiNPs that are produced from spark erosion in deionised water, with an average size distribution between 30 and 50nm as indicated by SEM analysis. Under optimised mixing conditions, 2g of purified SiNPs were mixed with 20g of alumina mu-particles (with an approximate diameter of 100 mu m), in the presence of ethanol and stirred thoroughly to form a slurry. The slurry is the then co-fired in an oxidation furnace, initially heated to 120 degrees C for 20minutes to evaporate the ethanol, and then re-uploaded again after compaction in a temperature of 1100 degrees C for 2hours, after which AACNS are obtained. Afterwards, shear bond strength tests are applied on zirconia ceramic bars, whose surface is modified by AACNS. The result shows that average bond strength is about 12MPa. This method also could be applied to prepare other kinds of abrasive coated by different nanoparticles for improving the bonding strength between coatings and substrates by the method of tribochemical.
关键词	Alumina abrasive coating resin bond strength silicon nanoparticles
DOI	10.1080/17458080.2018.1502478
收录类别	SCI
语种	英语
WOS研究方向	Chemistry ; Science & Technology - Other Topics ; Materials Science ; Physics
WOS类目	Chemistry, Multidisciplinary ; Nanoscience & Nanotechnology ; Materials Science, Multidisciplinary ; Physics, Applied
WOS记录号	WOS:000450583500001
出版者	TAYLOR & FRANCIS LTD
引用统计	被引频次：1[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/130490
专题	中国科学院金属研究所
通讯作者	Zhang Wei
作者单位	1.Changzhou Univ, Sch Mech Engn, Changzhou 213164, Jiangsu, Peoples R China 2.Changzhou High Technol Res Key Lab Mould Adv Mfg, Changzhou, Jiangsu, Peoples R China 3.Chinese Acad Sci, Inst Met Res, Shenyang, Liaoning, Peoples R China
推荐引用方式 GB/T 7714	Zhang Wei,Farooq, Ahmad,Wu Wangping,et al. Production of alumina micro abrasives coated with nano-silica for bonding improvements to zirconia[J]. JOURNAL OF EXPERIMENTAL NANOSCIENCE,2018,13(1):211-219.
APA	Zhang Wei,Farooq, Ahmad,Wu Wangping,&Kong Dejun.(2018).Production of alumina micro abrasives coated with nano-silica for bonding improvements to zirconia.JOURNAL OF EXPERIMENTAL NANOSCIENCE,13(1),211-219.
MLA	Zhang Wei,et al."Production of alumina micro abrasives coated with nano-silica for bonding improvements to zirconia".JOURNAL OF EXPERIMENTAL NANOSCIENCE 13.1(2018):211-219.