| Breakaway oxidation of a low-Al content nanocrystalline coating at 1000 degrees C | |
| Sun, Wenyao1,2; Chen, Minghui3; Bao, Zebin1; Wu, Changjun4; Zhu, Shenglong1,2; Wang, Fuihui1,3 | |
| Corresponding Author | Chen, Minghui(mhchen@mail.neu.edu.cn) ; Bao, Zebin(zbbao@imr.ac.cn) |
| 2019-01-25 | |
| Source Publication | SURFACE & COATINGS TECHNOLOGY
 |
| ISSN | 0257-8972 |
| Volume | 358Pages:958-967 |
| Abstract | Nanocrystalline coating though with low Al reservoir shows high oxidation and spallation resistance, owing to its high density of defects and grain boundaries. It now attracts growing attention. However, with oxidation going on, its stability is always a significant concern since such a high-temperature protective coating should be designed with a long life-expectancy when the nano-sized grains have grown and the reserved Al has been consumed a lot. Yet, this issue has never been clarified. To identify the exact mode of breakaway oxidation, a nanocrystalline coating was prepared with very low Al content that could decrease fast to a critical value in a very short oxidation time. Its oxidation behaviour related with the stability was studied in detail at 1000 degrees C. Results indicate that an intact external alumina scale still forms at the surface of the nanocrystalline coating initially. However, after 100 h exposure, grains growing and the continuous consuming of Al of the nanocrystalline coating lead to oxidation of Ti and doping of titanium oxide in the alumina scale, which was accompanied with the formation of abundant micropores and cracks. Thereafter, scale spalls off and abundant less-protective oxides, e.g. TiO2, NiCr2O4, NiTiO3, form, and breakaway oxidation occurs. |
| Keyword | Superalloys Nanocrystalline coating High-temperature oxidation |
| Funding Organization | National Natural Science Foundation of China ; Jiangsu Province Key Laboratory of Materials Surface Science and Technology |
| DOI | 10.1016/j.surfcoat.2018.12.034 |
| Indexed By | SCI |
| Language | 英语 |
| Funding Project | National Natural Science Foundation of China[51671053] ; Jiangsu Province Key Laboratory of Materials Surface Science and Technology[KFBM20170001] |
| WOS Research Area | Materials Science ; Physics |
| WOS Subject | Materials Science, Coatings & Films ; Physics, Applied |
| WOS ID | WOS:000456762300113 |
| Publisher | ELSEVIER SCIENCE SA |
| Citation statistics | |
| Document Type | 期刊论文 |
| Identifier | http://ir.imr.ac.cn/handle/321006/131343 |
| Collection | 中国科学院金属研究所 |
| Corresponding Author | Chen, Minghui; Bao, Zebin |
| Affiliation | 1.Chinese Acad Sci, Shenyang Natl Lab Mat Sci, Inst Met Res, Corros & Protect Div, Shenyang 110016, Liaoning, Peoples R China 2.Univ Sci & Technol China, Coll Mat Sci & Engn, Hefei 230026, Anhui, Peoples R China 3.Northeastern Univ, Shenyang Natl Lab Mat Sci, Corros & Protect Div, Shenyang 110819, Liaoning, Peoples R China 4.Changzhou Univ, Jiangsu Key Lab Mat Surface Sci & Technol, Changzhou 213164, Jiangsu, Peoples R China |
| Recommended Citation GB/T 7714 | Sun, Wenyao,Chen, Minghui,Bao, Zebin,et al. Breakaway oxidation of a low-Al content nanocrystalline coating at 1000 degrees C[J]. SURFACE & COATINGS TECHNOLOGY,2019,358:958-967. |
| APA | Sun, Wenyao,Chen, Minghui,Bao, Zebin,Wu, Changjun,Zhu, Shenglong,&Wang, Fuihui.(2019).Breakaway oxidation of a low-Al content nanocrystalline coating at 1000 degrees C.SURFACE & COATINGS TECHNOLOGY,358,958-967. |
| MLA | Sun, Wenyao,et al."Breakaway oxidation of a low-Al content nanocrystalline coating at 1000 degrees C".SURFACE & COATINGS TECHNOLOGY 358(2019):958-967. |
| Files in This Item: | There are no files associated with this item. | |||||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment