Characteristics and printability of K417G nickel-base alloy powder prepared by VIGA method

doi:10.1080/00325899.2018.1546921

IMR OpenIR

	Characteristics and printability of K417G nickel-base alloy powder prepared by VIGA method
	Jia, Wuming 1; Chen, Suiyuan 1; Wei, Mingwei 1; Liang, Jing 1; Liu, Changsheng 1; Li, Jinguo 2
通讯作者	Chen, Suiyuan(chensy@smm.neu.edu.cn)
	2019
发表期刊	POWDER METALLURGY
ISSN	0032-5899
卷号	62 期号:1 页码:30-37
摘要	Nickel-based K417G superalloy powder is the main material used in laser additive manufacturing (LAM) of aerospace engine turbine blades. In this study, K417G powder was prepared by the vacuum induction melting gas atomisation method (VIGA). Powder characteristics and microstructure were measured, and the properties of fabricated samples were studied. The results show that the powder mean particle size D-50 was 74 mu m, flowability was 16.6 s/50 g, apparent density was 4.78 g cm(-3), and the oxygen content of the powder was 0.015%. Powder and LAM sample microstructure consisted of gamma, gamma ', and carbide. The average microhardness was 410 HV, tensile strength was 1080 MPa, yield strength was 828 MPa and elongation was 13.52%. K417G superalloy powder prepared by VIGA method has potential for application in laser additive manufacturing.
关键词	LAM blades K417G powder VIGA method powder characteristics
资助者	National Natural Science Foundation of Liaoning United fund ; National Key R&D Program of China ; Research and development plan for the future emerging industries in Shenyang
DOI	10.1080/00325899.2018.1546921
收录类别	SCI
语种	英语
资助项目	National Natural Science Foundation of Liaoning United fund[U1508213] ; National Key R&D Program of China[2016YFB1100201] ; Research and development plan for the future emerging industries in Shenyang[18-004-2-26]
WOS研究方向	Metallurgy & Metallurgical Engineering
WOS类目	Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000458410800004
出版者	TAYLOR & FRANCIS LTD
引用统计	被引频次：4[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/131538
专题	中国科学院金属研究所
通讯作者	Chen, Suiyuan
作者单位	1.Northeastern Univ, Key Lab Anisotropy & Texture Mat, Minist Educ, Key Lab Laser Applicat Technol Liaoning Prov,Sch, 11 Lane 3,WenHua Rd, Shenyang, Liaoning, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang, Liaoning, Peoples R China
推荐引用方式 GB/T 7714	Jia, Wuming,Chen, Suiyuan,Wei, Mingwei,et al. Characteristics and printability of K417G nickel-base alloy powder prepared by VIGA method[J]. POWDER METALLURGY,2019,62(1):30-37.
APA	Jia, Wuming,Chen, Suiyuan,Wei, Mingwei,Liang, Jing,Liu, Changsheng,&Li, Jinguo.(2019).Characteristics and printability of K417G nickel-base alloy powder prepared by VIGA method.POWDER METALLURGY,62(1),30-37.
MLA	Jia, Wuming,et al."Characteristics and printability of K417G nickel-base alloy powder prepared by VIGA method".POWDER METALLURGY 62.1(2019):30-37.