High Temperature Oxidation Behaviors of Two Cast Ni-based Superalloys
Gao Shuang1,2; Hou Jieshan1; Yang Fei1; Wang Changshuai1; Zhou Lanzhang1
Corresponding AuthorHou Jieshan(jshou@imr.ac.cn)
2019-03-01
Source PublicationRARE METAL MATERIALS AND ENGINEERING
ISSN1002-185X
Volume48Issue:3Pages:960-966
AbstractHigh temperature oxidation behaviors of cast K317 and K325 alloy at 900 and 1000 degrees C in air environment were contrastively investigated by TGA, XRD and SEM (EDS). The results show that K317 alloy has a superior oxidation resistance compared with K325 alloy. The kinetic curves of the two alloys oxidized at 900 degrees C for 100 h obey the parabolic rate law while those at 1000 degrees C obey sectionally the parabolic rate law. The oxide structure of K317, from the top surface down to the base material, consists of NiO-TiO2-NiCr2O4 composite oxide, Cr2O3 oxide dense band and Al2O3 internal oxide. In comparison, internal oxidation is not observed in K325 alloy whose oxide layer is composed of two oxide layers: NiO-NiCr2O4-Nb2O5 composite oxide and Cr2O3 oxide layer. Serious MoO3 volatilization and oxide spallation take place in K325 alloy after the oxidation at 1000 degrees C for 100 h. In addition, the adhesion property of K325 alloy is worse than that of K317 alloy due to the occurrence of the micro-voids on the oxide layer/substrate interface.
KeywordNi-based superalloy anti-oxidation element oxidation kinetics oxidation mechanism
Indexed BySCI
Language英语
WOS Research AreaMaterials Science ; Metallurgy & Metallurgical Engineering
WOS SubjectMaterials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS IDWOS:000463845300041
PublisherNORTHWEST INST NONFERROUS METAL RESEARCH
Citation statistics
Cited Times:3[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/132879
Collection中国科学院金属研究所
Corresponding AuthorHou Jieshan
Affiliation1.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China
2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China
Recommended Citation
GB/T 7714
Gao Shuang,Hou Jieshan,Yang Fei,et al. High Temperature Oxidation Behaviors of Two Cast Ni-based Superalloys[J]. RARE METAL MATERIALS AND ENGINEERING,2019,48(3):960-966.
APA Gao Shuang,Hou Jieshan,Yang Fei,Wang Changshuai,&Zhou Lanzhang.(2019).High Temperature Oxidation Behaviors of Two Cast Ni-based Superalloys.RARE METAL MATERIALS AND ENGINEERING,48(3),960-966.
MLA Gao Shuang,et al."High Temperature Oxidation Behaviors of Two Cast Ni-based Superalloys".RARE METAL MATERIALS AND ENGINEERING 48.3(2019):960-966.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Gao Shuang]'s Articles
[Hou Jieshan]'s Articles
[Yang Fei]'s Articles
Baidu academic
Similar articles in Baidu academic
[Gao Shuang]'s Articles
[Hou Jieshan]'s Articles
[Yang Fei]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Gao Shuang]'s Articles
[Hou Jieshan]'s Articles
[Yang Fei]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.