Enhanced tensile and bending yield strengths of 304 stainless steel and H62 brass by surface spinning strengthening

doi:10.1016/j.msea.2019.03.113

IMR OpenIR

	Enhanced tensile and bending yield strengths of 304 stainless steel and H62 brass by surface spinning strengthening
	Ren, C. X.1,2; Wang, Q.1; Zhang, Z. J.1; Yang, H. J.1; Zhang, Z. F.1,2
通讯作者	Wang, Q.(gmwang@imr.ac.cn) ; Zhang, Z. F.(zhfzhang@imr.ac.cn)
	2019-04-29
发表期刊	MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
ISSN	0921-5093
卷号	754 页码:593-601
摘要	In this work, the tensile and bending yield strengths of 304 stainless steel and H62 brass are effectively enhanced by surface spinning strengthening (3S) that can introduce a strengthening layer with gradient microstructure on the samples. The results show that the two metals exhibit distinct grain refinement in the top layer as well as severe grain deformation in the subsurface layer with obvious gradient characteristics. For the tensile yield strength, it increases from 336 MPa to 372 MPa for 304 stainless steel, and 280 MPa-294 MPa for H62 brass, respectively. For the bending yield strength, it increases from 581 MPa to 667 MPa for 304 stainless steel, and 496 MPa-523 MPa for H62 brass, respectively. A two-phase (soft and hard phases) structure for the surface strengthened metals is proposed to analyze the enhancement of the tensile yield strength, and the enhancement of tensile yield strength is determined by the maximum microhardness and the thickness of the hardened layer. The enhancement of bending yield strength may be attributed to the maximum microhardness and the corresponding nano-scale grains in the topmost layer. Based on the results above, the tensile and bending yield strengths can be improved and optimized by constructing the gradient microstructure with different grain refinement and microhardness distributions.
关键词	304 stainless steel H62 brass Surface spinning strengthening Tension Three-point bending Strength
资助者	National Natural Science Foundation of China ; Innovation Fund for Graduate students of IMR.CAS
DOI	10.1016/j.msea.2019.03.113
收录类别	SCI
语种	英语
资助项目	National Natural Science Foundation of China[U1664253] ; National Natural Science Foundation of China[51331007] ; Innovation Fund for Graduate students of IMR.CAS
WOS研究方向	Science & Technology - Other Topics ; Materials Science ; Metallurgy & Metallurgical Engineering
WOS类目	Nanoscience & Nanotechnology ; Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000466249400059
出版者	ELSEVIER SCIENCE SA
引用统计	被引频次：31[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/133275
专题	中国科学院金属研究所
通讯作者	Wang, Q.; Zhang, Z. F.
作者单位	1.Chinese Acad Sci, Inst Met Res, Mat Fatigue & Fracture Div, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Anhui, Peoples R China
推荐引用方式 GB/T 7714	Ren, C. X.,Wang, Q.,Zhang, Z. J.,et al. Enhanced tensile and bending yield strengths of 304 stainless steel and H62 brass by surface spinning strengthening[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2019,754:593-601.
APA	Ren, C. X.,Wang, Q.,Zhang, Z. J.,Yang, H. J.,&Zhang, Z. F..(2019).Enhanced tensile and bending yield strengths of 304 stainless steel and H62 brass by surface spinning strengthening.MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,754,593-601.
MLA	Ren, C. X.,et al."Enhanced tensile and bending yield strengths of 304 stainless steel and H62 brass by surface spinning strengthening".MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING 754(2019):593-601.