Oxidation behaviors of Fe-25Cr-20Ni-chi Nb austenitic weld metals at 1100 degrees C in ambient air: Role of elemental niobium

doi:10.1016/j.corsci.2019.108137

IMR OpenIR

	Oxidation behaviors of Fe-25Cr-20Ni-chi Nb austenitic weld metals at 1100 degrees C in ambient air: Role of elemental niobium
	Zhang, Xu 1,2,3; Li, Dianzhong 1; Li, Yiyi 1; Lu, Shanping 1
通讯作者	Lu, Shanping(shplu@imr.ac.cn)
	2019-10-01
发表期刊	CORROSION SCIENCE
ISSN	0010-938X
卷号	159 页码:13
摘要	The isothermal oxidation behaviors of the Fe-25Cr-20Ni-chi Nb (0-1.6 wt.%) weld metals have been investigated in air at 1100 degrees C. Results showed that niobium has a detrimental effect on the elevated temperature oxidation resistance of the chromia-forming weld metals. In the Nb content range studied, the Nb content of 1.6 wt.% showed the most deleterious effect on the chromia layer. Niobium promoted the chromium depletion underneath the oxide/matrix interface by impeding the chromium diffusion, which ruined the compactness of the chromia layer. The oxidation of niobium at the oxide layer/metal interface can further cause severe damage to the chromia layer, resulting in catastrophic oxide spallation.
关键词	Austenitic weld metal SEM XRD High temperature corrosion Oxidation
资助者	Key Research Program of Chinese Academy of Sciences
DOI	10.1016/j.corsci.2019.108137
收录类别	SCI
语种	英语
资助项目	Key Research Program of Chinese Academy of Sciences[ZDRW-CN-2017-1]
WOS研究方向	Materials Science ; Metallurgy & Metallurgical Engineering
WOS类目	Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000488143500027
出版者	PERGAMON-ELSEVIER SCIENCE LTD
引用统计	被引频次：24[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/135627
专题	中国科学院金属研究所
通讯作者	Lu, Shanping
作者单位	1.Chinese Acad Sci, Shenyang Natl Lab Mat Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China 2.Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Shenyang 110014, Liaoning, Peoples R China 3.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Liaoning, Peoples R China
推荐引用方式 GB/T 7714	Zhang, Xu,Li, Dianzhong,Li, Yiyi,et al. Oxidation behaviors of Fe-25Cr-20Ni-chi Nb austenitic weld metals at 1100 degrees C in ambient air: Role of elemental niobium[J]. CORROSION SCIENCE,2019,159:13.
APA	Zhang, Xu,Li, Dianzhong,Li, Yiyi,&Lu, Shanping.(2019).Oxidation behaviors of Fe-25Cr-20Ni-chi Nb austenitic weld metals at 1100 degrees C in ambient air: Role of elemental niobium.CORROSION SCIENCE,159,13.
MLA	Zhang, Xu,et al."Oxidation behaviors of Fe-25Cr-20Ni-chi Nb austenitic weld metals at 1100 degrees C in ambient air: Role of elemental niobium".CORROSION SCIENCE 159(2019):13.