| Microstructure and Mechanical Performance of the DD98M-DD98M Single Crystal Superalloy Joints Brazed Using a Pd-Si Composite Filler | |
| Qin, Chunjie1; Xu, Haitao2; Zhou, Zhengqiang3; He, Yanming1,2; Lu, Chuanyang1,2; Gao, Ke1,2; Zheng, Wenjian1,2; Yang, Jianguo1,2; Wang, Donghong4; Sun, Yuan5; Gao, Zengliang1,2 | |
| Corresponding Author | He, Yanming(heyanming@zjut.edu.cn) ; Sun, Yuan(yuansun@imr.ac.cn) |
| 2019-09-01 | |
| Source Publication | METALS
 |
| Volume | 9Issue:9Pages:14 |
| Abstract | In this work, the DD98M single crystal superalloys were brazed to themselves using a Pd-Si composite filler. The effect of brazing temperature and soaking time on the microstructure and mechanical behavior of the joints was studied. The microstructure and phase constitution in the joint were identified by the SEM and EDS analysis. The results indicated that the joint obtained was constituted by DD98M/zone 2/zone 1/zone 2/DD98M. The zone 1 was primarily made up of the Ni (Pd, Cr, Co) (s.s), Pd4Si, Pd (Ni, Ti, Al) (s.s) and Pd-rich Ni (Pd, Cr, Co) (s.s), while the zone 2 consisted of the Ni (Pd, Cr, Co) (s.s) and Al2Pd5. During the brazing process, increasing the brazing temperature strengthened the fluidity of the liquid filler, which was favorable to eliminating the solidified pores in the brazing seam. Furthermore, a higher brazing temperature would cause the phases in the zones 1 and 2 to be coarsened remarkably. When setting the brazing temperature to 1060 degrees C, extending the soaking time made the amount of Pd (Ni, Ti, Al) (s.s) decrease, whereas the amount of Pd4Si increased, because the peritectic reaction between the Pd (Ni, Ti, Al) (s.s) and remnant liquid filler was enhanced. Among the brazing process parameters under investigation, the maximum joint average shear strength obtained reached 338 MPa when the joint was brazed at 1060 degrees C for 30 min. A ductile fracture mode happened during the shear tests under a joining condition. The work performed can provide valuable data to design the single crystal superalloy brazed joint. |
| Keyword | single crystal superalloy brazing microstructure shear strength |
| Funding Organization | National Natural Science Foundation of China ; Natural Science Foundation of Zhejiang Province |
| DOI | 10.3390/met9091001 |
| Indexed By | SCI |
| Language | 英语 |
| Funding Project | National Natural Science Foundation of China[51405439] ; National Natural Science Foundation of China[51705461] ; Natural Science Foundation of Zhejiang Province[LY17E050019] |
| WOS Research Area | Materials Science ; Metallurgy & Metallurgical Engineering |
| WOS Subject | Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
| WOS ID | WOS:000489129800087 |
| Publisher | MDPI |
| Citation statistics | |
| Document Type | 期刊论文 |
| Identifier | http://ir.imr.ac.cn/handle/321006/135639 |
| Collection | 中国科学院金属研究所 |
| Corresponding Author | He, Yanming; Sun, Yuan |
| Affiliation | 1.Zhejiang Univ Technol, Coll Mech Engn, Hangzhou 310014, Zhejiang, Peoples R China 2.Zhejiang Univ Technol, Inst Proc Equipment & Control Engn, Hangzhou 310014, Zhejiang, Peoples R China 3.Zhejiang Prov Elect Power Sci & Res Inst, Hangzhou 310014, Zhejiang, Peoples R China 4.Zhejiang Univ Technol, Sch Chem Engn, Hangzhou 310014, Zhejiang, Peoples R China 5.Chinese Acad Sci, Inst Met Res, Dept Superalloy, Shenyang 110016, Peoples R China |
| Recommended Citation GB/T 7714 | Qin, Chunjie,Xu, Haitao,Zhou, Zhengqiang,et al. Microstructure and Mechanical Performance of the DD98M-DD98M Single Crystal Superalloy Joints Brazed Using a Pd-Si Composite Filler[J]. METALS,2019,9(9):14. |
| APA | Qin, Chunjie.,Xu, Haitao.,Zhou, Zhengqiang.,He, Yanming.,Lu, Chuanyang.,...&Gao, Zengliang.(2019).Microstructure and Mechanical Performance of the DD98M-DD98M Single Crystal Superalloy Joints Brazed Using a Pd-Si Composite Filler.METALS,9(9),14. |
| MLA | Qin, Chunjie,et al."Microstructure and Mechanical Performance of the DD98M-DD98M Single Crystal Superalloy Joints Brazed Using a Pd-Si Composite Filler".METALS 9.9(2019):14. |
| Files in This Item: | There are no files associated with this item. | |||||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment