| Very high cycle fatigue behavior of bearing steel with rare earth addition | |
| Yang, Chaoyun1,2; Luan, Yikun1,2; Li, Dianzhong1,2; Li, Yiyi1,2; Tariq, Naeem ul Haq3,4 | |
| 通讯作者 | Luan, Yikun(ykluan@imr.ac.cn) ; Li, Dianzhong(dzli@imr.ac.cn) |
| 2020-02-01 | |
| 发表期刊 | INTERNATIONAL JOURNAL OF FATIGUE
 |
| ISSN | 0142-1123 |
| 卷号 | 131页码:13 |
| 摘要 | This study aims to clarify the effect of rare earth (RE) addition on the very high cycle fatigue (VHCF) behavior of high-carbon chromium bearing steel. For this purpose, ultrasonic tension-compression fatigue tests were carried out on specimens extracted from bearing steels with and without RE addition. As a result, RE addition can prolong the fatigue life of bearing steel over 10 times and improve the fatigue limit at 10(9) cycles by 9.4% from 720 MPa to 788 MPa, which mainly result from the modification of RE elements to common CaO-Al2O3-MgOSiO2-CaS inclusions, forming complex RE inclusions and leading to the decrease of inclusion size and the volume fraction of inclusions in bearing steel with RE addition. On the VHCF fracture of bearing steels with and without RE addition, both internal cracking mode and interface cracking mode exist at inclusions. Compared with bearing steel with RE addition, bearing steel without RE addition exhibits a longer crack initiation life due to stronger internal binding force of complex inclusions and interfacial binding force between complex inclusions and the matrix. However, smaller complex RE inclusions make crack propagation life of the former significantly longer than that of the latter. In addition, fine granular area (FGA) can be used to estimate the fatigue limit of different fatigue life in the VHCF regime and the fatigue limit at 10(9) cycles evaluated based on FGA indicates an error of around 2% with respect to the fatigue limit measured by staircase method. |
| 关键词 | Very high cycle fatigue Bearing steel Rare earth Inclusions Crack initiation and propagation |
| 资助者 | National Natural Science Foundation of China |
| DOI | 10.1016/j.ijfatigue.2019.105263 |
| 收录类别 | SCI |
| 语种 | 英语 |
| 资助项目 | National Natural Science Foundation of China[U1708252] |
| WOS研究方向 | Engineering ; Materials Science |
| WOS类目 | Engineering, Mechanical ; Materials Science, Multidisciplinary |
| WOS记录号 | WOS:000504505600011 |
| 出版者 | ELSEVIER SCI LTD |
| 引用统计 | |
| 文献类型 | 期刊论文 |
| 条目标识符 | http://ir.imr.ac.cn/handle/321006/136524 |
| 专题 | 中国科学院金属研究所 |
| 通讯作者 | Luan, Yikun; Li, Dianzhong |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Anhui, Peoples R China 3.Univ Chinese Acad Sci, Beijing 100049, Peoples R China 4.Pakistan Inst Engn & Appl Sci, Dept Met & Mat Engn, Islamabad, Pakistan |
| 推荐引用方式 GB/T 7714 | Yang, Chaoyun,Luan, Yikun,Li, Dianzhong,et al. Very high cycle fatigue behavior of bearing steel with rare earth addition[J]. INTERNATIONAL JOURNAL OF FATIGUE,2020,131:13. |
| APA | Yang, Chaoyun,Luan, Yikun,Li, Dianzhong,Li, Yiyi,&Tariq, Naeem ul Haq.(2020).Very high cycle fatigue behavior of bearing steel with rare earth addition.INTERNATIONAL JOURNAL OF FATIGUE,131,13. |
| MLA | Yang, Chaoyun,et al."Very high cycle fatigue behavior of bearing steel with rare earth addition".INTERNATIONAL JOURNAL OF FATIGUE 131(2020):13. |
| 条目包含的文件 | 条目无相关文件。 | |||||
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论