Effect of Orientation Deviation on Microstructure and Mechanical Properties of Nickel-Based Single Crystal Superalloy Brazing Joints
Zhao Xu1,2; Sun Yuan2; Hou Xingyu2; Zhang Hongyu2; Zhou Yizhou1,2; Ding Yutian1
Corresponding AuthorSun Yuan(yuansun@imr.ac.cn) ; Zhou Yizhou(yzzhou@imr.ac.cn)
2020-02-11
Source PublicationACTA METALLURGICA SINICA
ISSN0412-1961
Volume56Issue:2Pages:171-181
AbstractNi-based single crystal superalloy has excellent high temperature properties, which is the main materials for aero-engine turbine blade. In order to improve the yield strength of single crystal blades, the reliable bonding technology has become an increasingly indispensable key technology in the process of producing single crystal blades. However, there is inevitably an orientation deviation in the bonded single crystal component, owing to its shape complexity and randomness during assembly practice of bonding single crystal components. The CMSX-4 single crystal superalloy with the orientation combination of 0 degrees+0 degrees, 0 degrees+45 degrees and 0 degrees+90 degrees were brazed by Ni-based filler alloy at 1210 degrees C for 30 min and carried out ageing heat treatment. The effect of base material orientation combination on the microstructure was analyzed by SEM, EBSD and EPMA. The mechanical properties of joints after bonding and ageing treatment were tested. The result indicates that the microstructures and phase compositions of three orientation combination joints were similar in the filler alloy zone, consisting of gamma-Ni, gamma', gamma+gamma' eutectic, M3B2 type boride, CrB, nickel-silicon compound and gamma-Ni+Ni3B+CrB ternary eutectic phase. The melting point depressant B in the filler alloy is not diffused significantly to the base material, and no brittle compound phase is precipitated in the diffusion affected zone of the joint. After ageing treatment, elements diffusion is uniform and brittle precipitates are reduced, and the continuous grain boundary can be observed at the center of the joint when the base material on both sides of the joint has orientation deviation. The testing results of mechanical properties show that the base material orientation deviation has no distinctly effect on the room and high temperature tensile properties of the joint. However, the tensile strengths of the joint at room and high temperature both reduce with orientation deviation after ageing treatment, but the degree of orientation deviation has no obvious influence on the tensile strength of the joint. The fracture of the three joints occurs in the filler alloy zone.
Keywordsingle crystal superalloy orientation deviation nickel-based filler alloy brazing
Funding OrganizationNational Youth Science Fund Project of China
DOI10.11900/0412.1961.2019.00258
Indexed BySCI
Language英语
Funding ProjectNational Youth Science Fund Project of China[51801206]
WOS Research AreaMetallurgy & Metallurgical Engineering
WOS SubjectMetallurgy & Metallurgical Engineering
WOS IDWOS:000507327100005
PublisherSCIENCE PRESS
Citation statistics
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/136615
Collection中国科学院金属研究所
Corresponding AuthorSun Yuan; Zhou Yizhou
Affiliation1.Lanzhou Univ Technol, State Key Lab Adv & Recycling Nonferrous Met, Lanzhou 730050, Peoples R China
2.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China
Recommended Citation
GB/T 7714
Zhao Xu,Sun Yuan,Hou Xingyu,et al. Effect of Orientation Deviation on Microstructure and Mechanical Properties of Nickel-Based Single Crystal Superalloy Brazing Joints[J]. ACTA METALLURGICA SINICA,2020,56(2):171-181.
APA Zhao Xu,Sun Yuan,Hou Xingyu,Zhang Hongyu,Zhou Yizhou,&Ding Yutian.(2020).Effect of Orientation Deviation on Microstructure and Mechanical Properties of Nickel-Based Single Crystal Superalloy Brazing Joints.ACTA METALLURGICA SINICA,56(2),171-181.
MLA Zhao Xu,et al."Effect of Orientation Deviation on Microstructure and Mechanical Properties of Nickel-Based Single Crystal Superalloy Brazing Joints".ACTA METALLURGICA SINICA 56.2(2020):171-181.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Zhao Xu]'s Articles
[Sun Yuan]'s Articles
[Hou Xingyu]'s Articles
Baidu academic
Similar articles in Baidu academic
[Zhao Xu]'s Articles
[Sun Yuan]'s Articles
[Hou Xingyu]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Zhao Xu]'s Articles
[Sun Yuan]'s Articles
[Hou Xingyu]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.