Effect of Cl- Concentration on the SCC Behavior of 13Cr Stainless Steel in High-Pressure CO2 Environment

doi:10.1007/s40195-019-00923-1

IMR OpenIR

	Effect of Cl- Concentration on the SCC Behavior of 13Cr Stainless Steel in High-Pressure CO2 Environment
	Zhao, Jin-Jin 1,2; Liu, Xian-Bin 1; Hu, Shuai 1,2; Han, En-Hou 1
通讯作者	Liu, Xian-Bin(xbliu@imr.ac.cn)
	2019-12-01
发表期刊	ACTA METALLURGICA SINICA-ENGLISH LETTERS
ISSN	1006-7191
卷号	32 期号:12 页码:1459-1469
摘要	An effect of Cl- concentration on the stress corrosion cracking (SCC) behavior of 13Cr stainless steel was investigated by employing electrochemical measurements and the slow strain rate tensile tests. These tests were conducted in various solutions with different concentrations of NaCl at 90 degrees C under 3 MPa CO2 with 3 MPa N-2. The results indicate that the passive film of the specimen formed in the 10% NaCl solution has the best protective effect on the matrix. The SCC susceptibility does not increase with increasing the chloride ion concentration, the lowest SCC susceptibility occurs when the NaCl concentration is 10%, and the specimens show higher SCC susceptibility in the 5% NaCl and 20% NaCl solutions.
关键词	13Cr Cl- Stress corrosion cracking CO2 environment
资助者	National Natural Science Foundation of China
DOI	10.1007/s40195-019-00923-1
收录类别	SCI
语种	英语
资助项目	National Natural Science Foundation of China[51501199]
WOS研究方向	Metallurgy & Metallurgical Engineering
WOS类目	Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000495116000003
出版者	CHINESE ACAD SCIENCES, INST METAL RESEARCH
引用统计	被引频次：4[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/137010
专题	中国科学院金属研究所
通讯作者	Liu, Xian-Bin
作者单位	1.Chinese Acad Sci, Natl Engn Ctr Corros Control, Inst Met Res, 62 Wencui Rd, Shenyang 110016, Liaoning, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei, Anhui, Peoples R China
推荐引用方式 GB/T 7714	Zhao, Jin-Jin,Liu, Xian-Bin,Hu, Shuai,et al. Effect of Cl- Concentration on the SCC Behavior of 13Cr Stainless Steel in High-Pressure CO2 Environment[J]. ACTA METALLURGICA SINICA-ENGLISH LETTERS,2019,32(12):1459-1469.
APA	Zhao, Jin-Jin,Liu, Xian-Bin,Hu, Shuai,&Han, En-Hou.(2019).Effect of Cl- Concentration on the SCC Behavior of 13Cr Stainless Steel in High-Pressure CO2 Environment.ACTA METALLURGICA SINICA-ENGLISH LETTERS,32(12),1459-1469.
MLA	Zhao, Jin-Jin,et al."Effect of Cl- Concentration on the SCC Behavior of 13Cr Stainless Steel in High-Pressure CO2 Environment".ACTA METALLURGICA SINICA-ENGLISH LETTERS 32.12(2019):1459-1469.