Versatility of potential protective layer material Ti2AlC on resisting CMAS corrosion to thermal barrier coatings

doi:10.1016/j.corsci.2020.108532

IMR OpenIR

	Versatility of potential protective layer material Ti2AlC on resisting CMAS corrosion to thermal barrier coatings
	Yan, Zheng 1; Guo, Lei 1,2; Zhang, Zhao 3; Wang, Xiaohui 4; Ye, Fuxing 1,2
通讯作者	Guo, Lei(glei028@tju.edu.cn)
	2020-05-01
发表期刊	CORROSION SCIENCE
ISSN	0010-938X
卷号	167 页码:14
摘要	Alleviating calcium-magnesium-alumina-silicate (CMAS) hazard to thermal barrier coatings (TBCs) has attracted increasing attentions. Here, we demonstrate that Ti2AlC is a promising protective layer material for TBCs against CMAS attack, and clarify its corrosion resistance mechanisms. The results reveal that pre-oxidized Ti2AlC has obvious advantages over its non-oxidized counterpart on promoting CMAS crystallization and inhibiting the melt infiltration. Pre-oxidation produces a continuous Al2O3 layer and TiO2 particles on Ti2AlC surface, and Al2O3 reacts with molten CMAS to form anorthite crystals, while TiO2, in the form of either Ti-rich particles or Ti dissolution (there is a content threshold), promotes the crystallization.
关键词	Thermal barrier coatings (TBCs) Calcium-magnesium-alumina-silicate (CMAS) Ti2AlC Pre-oxidization Crystallization mechanism
资助者	National Natural Science Foundation of China
DOI	10.1016/j.corsci.2020.108532
收录类别	SCI
语种	英语
资助项目	National Natural Science Foundation of China[51971156]
WOS研究方向	Materials Science ; Metallurgy & Metallurgical Engineering
WOS类目	Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000525869800042
出版者	PERGAMON-ELSEVIER SCIENCE LTD
引用统计	被引频次：29[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/138325
专题	中国科学院金属研究所
通讯作者	Guo, Lei
作者单位	1.Tianjin Univ, Sch Mat Sci & Engn, Tianjin 300072, Peoples R China 2.Minist Educ, Key Lab Adv Ceram & Machining Technol, Tianjin Key Lab Adv Joining Technol, Tianjin 300072, Peoples R China 3.Liaocheng Univ, Sch Mat Sci & Engn, Liaocheng 252059, Shandong, Peoples R China 4.Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China
推荐引用方式 GB/T 7714	Yan, Zheng,Guo, Lei,Zhang, Zhao,et al. Versatility of potential protective layer material Ti2AlC on resisting CMAS corrosion to thermal barrier coatings[J]. CORROSION SCIENCE,2020,167:14.
APA	Yan, Zheng,Guo, Lei,Zhang, Zhao,Wang, Xiaohui,&Ye, Fuxing.(2020).Versatility of potential protective layer material Ti2AlC on resisting CMAS corrosion to thermal barrier coatings.CORROSION SCIENCE,167,14.
MLA	Yan, Zheng,et al."Versatility of potential protective layer material Ti2AlC on resisting CMAS corrosion to thermal barrier coatings".CORROSION SCIENCE 167(2020):14.