Carbide precipitation behavior and mechanical properties of micro-alloyed medium Mn steel

doi:10.1016/j.jmst.2019.12.024

IMR OpenIR

	Carbide precipitation behavior and mechanical properties of micro-alloyed medium Mn steel
	Hao, Luhan 1; Ji, Xiang 1,2; Zhang, Guangqian 1; Zhao, Wei 1; Sun, Mingyue 2; Peng, Yan 1
通讯作者	Sun, Mingyue(mysun@imr.ac.cn) ; Peng, Yan(pengyan@ysu.edu.cn)
	2020-06-15
发表期刊	JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
ISSN	1005-0302
卷号	47 页码:122-130
摘要	The carbide precipitation behavior and mechanical properties of advanced high strength steel deformed at different temperatures are investigated by X-ray diffractometer (XRD), scanning electron microscope (SEM), transmission electron microscope (TEM) equipped with an energy dispersing spectroscopy (EDS), and tensile tests. The medium Mn steel was subjected to controlled deformation up to 70% at 750 degrees C, 850 degrees C, 950 degrees C, and 1050 degrees C, and then quenched with water to room temperature, followed by intercritical annealing at 630 degrees C for 10 min. In comparison with the undeformed and quenched specimen, it can be concluded that acicular cementite precipitates during the quenching and cooling process, while granular NbC is the deformation induced precipitate and grows during the following annealing process. As the deformation temperature increases from 750 degrees C to 1050 degrees C, the product of strength and elongation increases at first and then decreases. The smallest average size of second phase particles (20 nm) and the best mechanical properties (32.5 GPa.%) can be obtained at the deformation temperature of 950 degrees C. (C) 2020 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.
关键词	Advanced high strength steel Medium Mn steel Thermal deformation Intercritical annealing The product of strength and elongation
资助者	National Key Research and Development Program ; National Natural Science Foundation of China ; National Science and Technology Major Project of China ; Key Program of the Chinese Academy of Sciences ; KeyProgram of Natural Science Foundation of Hebei Province of China ; CAS Interdisciplinary Innovation Team
DOI	10.1016/j.jmst.2019.12.024
收录类别	SCI
语种	英语
资助项目	National Key Research and Development Program[2018YFA0702900] ; National Natural Science Foundation of China[U1508215] ; National Natural Science Foundation of China[51774265] ; National Science and Technology Major Project of China[2019ZX06004010] ; Key Program of the Chinese Academy of Sciences[ZDRW-CN-2017-1] ; KeyProgram of Natural Science Foundation of Hebei Province of China[E2017203161] ; CAS Interdisciplinary Innovation Team
WOS研究方向	Materials Science ; Metallurgy & Metallurgical Engineering
WOS类目	Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000526956900013
出版者	JOURNAL MATER SCI TECHNOL
引用统计	被引频次：15[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/138475
专题	中国科学院金属研究所
通讯作者	Sun, Mingyue; Peng, Yan
作者单位	1.Yanshan Univ, Natl Engn Res Ctr Equipment & Technol Cold Strip, Qinhuangdao 066004, Hebei, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, 72 Wenhua Rd, Shenyang 110016, Peoples R China
推荐引用方式 GB/T 7714	Hao, Luhan,Ji, Xiang,Zhang, Guangqian,et al. Carbide precipitation behavior and mechanical properties of micro-alloyed medium Mn steel[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,2020,47:122-130.
APA	Hao, Luhan,Ji, Xiang,Zhang, Guangqian,Zhao, Wei,Sun, Mingyue,&Peng, Yan.(2020).Carbide precipitation behavior and mechanical properties of micro-alloyed medium Mn steel.JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,47,122-130.
MLA	Hao, Luhan,et al."Carbide precipitation behavior and mechanical properties of micro-alloyed medium Mn steel".JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY 47(2020):122-130.