Effect of Pt-Al bond-coat on the tensile deformation and fracture behaviors of a second-generation SX Ni-based superalloy at elevated temperatures

doi:10.1016/j.surfcoat.2020.125640

IMR OpenIR

	Effect of Pt-Al bond-coat on the tensile deformation and fracture behaviors of a second-generation SX Ni-based superalloy at elevated temperatures
	Tao, X. P.1,2; Wang, X. G.1; Zhou, Y. Z.1; Tan, K. J.1,2; Liang, J. J.1; Yang, Y. H.1; Liu, J. L.1; Liu, J. D.1; Li, J. G.1; Sun, X. F.1
通讯作者	Wang, X. G.(xgwang11b@imr.ac.cn) ; Zhou, Y. Z.(yzzhou@imr.ac.cn)
	2020-05-15
发表期刊	SURFACE & COATINGS TECHNOLOGY
ISSN	0257-8972
卷号	389 页码:11
摘要	An investigation was conducted into the influence of applying Pt-Al bond-coat on the tensile deformation and fracture behavior of second-generation single crystal superalloy substrate with the temperature ranging between room temperature RT and 1100 degrees C. In the meantime, the development of a two-layer Pt-Al bond-coat, consisting of an outer layer of single-phase beta-(Ni,Pt)Al and an inter-diffusion zone of refractory metal precipitates, has also been discussed. As revealed by the results, the application of Pt-Al bond-coat contributed to a noticeable deterioration in both yield strength and ultimate tensile strength of the superalloy substrate at elevated temperatures. Nevertheless, the elongation of coated superalloy was shown to be 17.2% (at RT) and 10.4% (at 750 degrees C) lower and 9.6% (at 1100 degrees C) higher compared to uncoated samples. Following tensile test, the TEM analyses indicated that there were onsets of various slip systems, the traditional superlattice stacking faults were retarded at intermediate temperature and the dislocation debris could be increased to develop dislocation networks at higher temperature in the region of superalloy near the bond-coat. As the temperature was on the rise, the fracture mechanism of coated superalloy shifted from tearing ridges and dimples to quasi-cleavage and then to micro-void coalescence. While that of Pt-Al bond-coat was transformed from brittle to ductile rupture. Within the temperature range from RT up to 750 degrees C, a combination of long crack lengths and greater crack penetration depths into bond-coat caused more deterioration in the tensile properties of superalloy. When the temperature rose above 750 degrees C, the application of Pt-Al bond-coat improved the ductility of the substrate, as a result of the ductile failure in the bond-coat which hindered the development of through-thickness cracks.
关键词	Pt-Al bond-coat Tensile deformation Fracture behaviors Ni-based superalloy Elevated temperatures
资助者	National Science and Technology Major Project ; National Key Research and Development Program of China ; National Natural Science Foundation of China (NSFC) ; State Key Lab of Advanced Metals and Materials Open Fund ; Youth Innovation Promotion Association, Chinese Academy of Sciences
DOI	10.1016/j.surfcoat.2020.125640
收录类别	SCI
语种	英语
资助项目	National Science and Technology Major Project[2017-VI-0002-0072] ; National Key Research and Development Program of China[2017YFA0700704] ; National Natural Science Foundation of China (NSFC)[51601192] ; National Natural Science Foundation of China (NSFC)[51671188] ; State Key Lab of Advanced Metals and Materials Open Fund[2018Z07] ; Youth Innovation Promotion Association, Chinese Academy of Sciences
WOS研究方向	Materials Science ; Physics
WOS类目	Materials Science, Coatings & Films ; Physics, Applied
WOS记录号	WOS:000528194000025
出版者	ELSEVIER SCIENCE SA
引用统计	被引频次：18[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/138635
专题	中国科学院金属研究所
通讯作者	Wang, X. G.; Zhou, Y. Z.
作者单位	1.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Peoples R China
推荐引用方式 GB/T 7714	Tao, X. P.,Wang, X. G.,Zhou, Y. Z.,et al. Effect of Pt-Al bond-coat on the tensile deformation and fracture behaviors of a second-generation SX Ni-based superalloy at elevated temperatures[J]. SURFACE & COATINGS TECHNOLOGY,2020,389:11.
APA	Tao, X. P..,Wang, X. G..,Zhou, Y. Z..,Tan, K. J..,Liang, J. J..,...&Sun, X. F..(2020).Effect of Pt-Al bond-coat on the tensile deformation and fracture behaviors of a second-generation SX Ni-based superalloy at elevated temperatures.SURFACE & COATINGS TECHNOLOGY,389,11.
MLA	Tao, X. P.,et al."Effect of Pt-Al bond-coat on the tensile deformation and fracture behaviors of a second-generation SX Ni-based superalloy at elevated temperatures".SURFACE & COATINGS TECHNOLOGY 389(2020):11.