Effects of Ta on the high temperature oxidation behavior of IN617 alloy in air

doi:10.1016/j.corsci.2020.108682

IMR OpenIR

	Effects of Ta on the high temperature oxidation behavior of IN617 alloy in air
	Gao, Shuang 1,2; He, Bo 1,2; Zhou, Lanzhang 3; Hou, Jieshan 3
通讯作者	He, Bo(jdhebo@163.com) ; Hou, Jieshan(jshou@imr.ac.cn)
	2020-07-01
发表期刊	CORROSION SCIENCE
ISSN	0010-938X
卷号	170 页码:7
摘要	Effects of Ta on the oxidation behavior of IN617 alloy were investigated by isothermal oxidation tests in air at 900 degrees C and 1000 degrees C. The oxidation resistance was improved with Ta content increasing. The Ta addition induced the formation of TaO2 at both temperatures. Ta was found to impede the out-diffusion of Ti resulting in the formation of TiO2 at the interface between outer Cr2O3 layer and metal substrate. TiO2 and TaO2 filled the voids inside Cr2O3 layer, which was the reason for the improved density of Cr2O3 scale in Ta-added alloys. Moreover, Ta inhibited the coarsening of inner Al2O3 oxides.
关键词	Ni-based superalloy Ta element Oxidation resistance Oxidation mechanism
资助者	Shanghai Science and Technology Committee Innovation Grant ; Shanghai Sailing Program
DOI	10.1016/j.corsci.2020.108682
收录类别	SCI
语种	英语
资助项目	Shanghai Science and Technology Committee Innovation Grant[17JC1400600] ; Shanghai Sailing Program[19YF1417500]
WOS研究方向	Materials Science ; Metallurgy & Metallurgical Engineering
WOS类目	Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000533523500020
出版者	PERGAMON-ELSEVIER SCIENCE LTD
引用统计	被引频次：51[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/138841
专题	中国科学院金属研究所
通讯作者	He, Bo; Hou, Jieshan
作者单位	1.Shanghai Univ Engn Sci, Sch Mat Engn, Shanghai 201620, Peoples R China 2.Shanghai Univ Engn Sci, Res Ctr High Temp Alloy Precis Forming, Shanghai 201620, Peoples R China 3.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China
推荐引用方式 GB/T 7714	Gao, Shuang,He, Bo,Zhou, Lanzhang,et al. Effects of Ta on the high temperature oxidation behavior of IN617 alloy in air[J]. CORROSION SCIENCE,2020,170:7.
APA	Gao, Shuang,He, Bo,Zhou, Lanzhang,&Hou, Jieshan.(2020).Effects of Ta on the high temperature oxidation behavior of IN617 alloy in air.CORROSION SCIENCE,170,7.
MLA	Gao, Shuang,et al."Effects of Ta on the high temperature oxidation behavior of IN617 alloy in air".CORROSION SCIENCE 170(2020):7.