Synergistic effect between cavitation erosion and corrosion for various copper alloys in sulphide-containing 3.5% NaCl solutions

doi:10.1016/j.wear.2020.203258

IMR OpenIR

	Synergistic effect between cavitation erosion and corrosion for various copper alloys in sulphide-containing 3.5% NaCl solutions
	Song, Q. N.1; Tong, Y.1; Xu, N.1; Sun, S. Y.1; Li, H. L.1; Bao, Y. F.1; Jiang, Y. F.1; Wang, Z. B.2; Qiao, Y. X.3
Corresponding Author	Song, Q. N.(qnsong@hhu.edu.cn)
	2020-06-15
Source Publication	WEAR
ISSN	0043-1648
Volume	450 Pages:11
Abstract	Cavitation erosion-corrosion (CE-C) behaviour of various copper alloys for ship propellers were investigated in sulphide-containing 3.5% NaCl solutions. Results indicate that the CE-C resistance remarkably decreases with increase in sulphide concentration for cast and friction stir processed nickel-aluminum bronzes. CE increases the current density by approximately two orders of magnitude and causes a positive potential shift when the sulphide concentration exceeds 50 ppm. The synergistic effect between CE and corrosion contributes greatly to CE-C degradation in sulphide solutions. However, the CE-C behaviour is insensitive to sulphide concentration for manganese-aluminum bronze and manganese brass. In all solutions, CE causes a positive potential shift and increases the current density by less than one order of magnitude. Mechanical attack dominates the CE-C damage.
Keyword	Copper alloy Sulphide Cavitation erosion Synergy
Funding Organization	National Natural Science Foundation of China ; Natural Science Foundation of Jiangsu Province ; Changzhou Sci Tech Program ; Fundamental Research Funds for the Central Universities
DOI	10.1016/j.wear.2020.203258
Indexed By	SCI
Language	英语
Funding Project	National Natural Science Foundation of China[51601058] ; National Natural Science Foundation of China[51879089] ; Natural Science Foundation of Jiangsu Province[BK20191161] ; Changzhou Sci Tech Program[CJ 20180045] ; Fundamental Research Funds for the Central Universities[2018B48614]
WOS Research Area	Engineering ; Materials Science
WOS Subject	Engineering, Mechanical ; Materials Science, Multidisciplinary
WOS ID	WOS:000531497200001
Publisher	ELSEVIER SCIENCE SA
Citation statistics	Cited Times:55[WOS] [WOS Record] [Related Records in WOS]
Document Type	期刊论文
Identifier	http://ir.imr.ac.cn/handle/321006/138862
Collection	中国科学院金属研究所
Corresponding Author	Song, Q. N.
Affiliation	1.Hohai Univ, Coll Mech & Elect Engn, 200 Jinling North Rd, Changzhou 213022, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, 62 Wencui Rd, Shenyang 110016, Peoples R China 3.Jiangsu Univ Sci & Technol, Coll Mat Sci & Engn, 2 Mengxi Rd, Zhenjiang 212003, Jiangsu, Peoples R China
Recommended Citation GB/T 7714	Song, Q. N.,Tong, Y.,Xu, N.,et al. Synergistic effect between cavitation erosion and corrosion for various copper alloys in sulphide-containing 3.5% NaCl solutions[J]. WEAR,2020,450:11.
APA	Song, Q. N..,Tong, Y..,Xu, N..,Sun, S. Y..,Li, H. L..,...&Qiao, Y. X..(2020).Synergistic effect between cavitation erosion and corrosion for various copper alloys in sulphide-containing 3.5% NaCl solutions.WEAR,450,11.
MLA	Song, Q. N.,et al."Synergistic effect between cavitation erosion and corrosion for various copper alloys in sulphide-containing 3.5% NaCl solutions".WEAR 450(2020):11.

Files in This Item:
There are no files associated with this item.

If you have any objections to this item, please fill out the form below and the administrator will contact you as soon as possible.
Content:
Email：	*
Institution:
Verification Code:	Refresh

Any comments and suggestions are welcomed.
Title:	*
Content:
Email：	*
Verification Code:	Refresh

中国科学院金属研究所机构知识库