Synergistic effect of corrosion and wear of the 316 stainless steel in molten zinc alloy at 460 degrees C

doi:10.1016/j.corsci.2019.108411

IMR OpenIR

	Synergistic effect of corrosion and wear of the 316 stainless steel in molten zinc alloy at 460 degrees C
	Yu, Zhongdi 1,2; Chen, Minghui 1,2; Li, Fengjie 1,2; Zhu, Shenglong 3; Wang, Fuhui 1,2
通讯作者	Chen, Minghui(mhchen@mail.neu.edu.cn)
	2020-04-01
发表期刊	CORROSION SCIENCE
ISSN	0010-938X
卷号	165 页码:10
摘要	The failure of 316 stainless steel under tribo-corrosion in molten zinc alloy (Zn-0.2Al, wt%) at 460 degrees C was investigated and compared with corrosion or the sole wear. In the absence of wear, intact Fe2Al5Znx layer forms and protects the steel from dramatic corrosion. Without liquid-metal corrosion, the steel suffers from plastic deformation on friction and slight adhesive wear. While for tribo-corrosion, the synergy of corrosion and wear accounts for 90 % of material loss. Firstly, corrosion generates a brittle scale and leads to embrittlement at subsurface, which accelerate wear. Secondly, wear promotes the formation of less-protective FeZn10 scale, accelerating corrosion.
关键词	Stainless steel Molten zinc alloy EPMA Liquid-metal corrosion Tribo-corrosion
资助者	National Key R&D Program of China ; National Natural Science Foundation of China ; Fundamental Research Funds for the Central Universities
DOI	10.1016/j.corsci.2019.108411
收录类别	SCI
语种	英语
资助项目	National Key R&D Program of China[2017YFB0306100] ; National Natural Science Foundation of China[51871051] ; Fundamental Research Funds for the Central Universities[N180212008]
WOS研究方向	Materials Science ; Metallurgy & Metallurgical Engineering
WOS类目	Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000518488800043
出版者	PERGAMON-ELSEVIER SCIENCE LTD
引用统计	被引频次：22[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/138972
专题	中国科学院金属研究所
通讯作者	Chen, Minghui
作者单位	1.Northeastern Univ, Shenyang Natl Lab Mat Sci, Shenyang 110819, Peoples R China 2.Northeastern Univ, Sch Mat Sci & Engn, Shenyang 110819, Peoples R China 3.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China
推荐引用方式 GB/T 7714	Yu, Zhongdi,Chen, Minghui,Li, Fengjie,et al. Synergistic effect of corrosion and wear of the 316 stainless steel in molten zinc alloy at 460 degrees C[J]. CORROSION SCIENCE,2020,165:10.
APA	Yu, Zhongdi,Chen, Minghui,Li, Fengjie,Zhu, Shenglong,&Wang, Fuhui.(2020).Synergistic effect of corrosion and wear of the 316 stainless steel in molten zinc alloy at 460 degrees C.CORROSION SCIENCE,165,10.
MLA	Yu, Zhongdi,et al."Synergistic effect of corrosion and wear of the 316 stainless steel in molten zinc alloy at 460 degrees C".CORROSION SCIENCE 165(2020):10.