Effect of Pt-rich position on the hot corrosion behavior of NiCoCrAlY coating for a single-crystal superalloy

doi:10.1016/j.surfcoat.2020.125938

IMR OpenIR

	Effect of Pt-rich position on the hot corrosion behavior of NiCoCrAlY coating for a single-crystal superalloy
	Yang, Y. F.1; Ren, P.1; Bao, Z. B.2; Zhu, S. L.2; Wang, F. H.3; Li, W.1
通讯作者	Yang, Y. F.(yfyang@jnu.edu.cn) ; Ren, P.(renp@foxmail.com)
	2020-08-15
发表期刊	SURFACE & COATINGS TECHNOLOGY
ISSN	0257-8972
卷号	395 页码:10
摘要	Two Pt modified NiCoCrAlY coatings were prepared with the Pt-rich zone located at the coating surface (NiCoCrAlY + Pt) or at the substrate/coating interface (Pt + NiCoCrAlY). The microstructures of two coatings were studied with TEM. The hot corrosion performance of the coatings was investigated in Na2SO4/NaCl (75:25, wt./wt.) mixed salt at 900 degrees C in comparison with the plain NiCoCrAlY coating. The results revealed that the NiCoCrAl + Pt coating showed superior hot corrosion resistance due to higher Al content at the surface and merits of Pt in improving oxide scale adhesion. Ta was constrained beneath the coating/substrate interface in Pt + NiCoCrAlY coating owing to the strong affinity between Pt and Ta.
关键词	Pt-modification NiCoCrAlY Hot corrosion TEM EPMA
资助者	Science and Technology Program of Guangzhou ; Fundamental Research Funds for the Central Universities ; Scientific Research Funds for the Talents and Innovation Foundation of Jinan University
DOI	10.1016/j.surfcoat.2020.125938
收录类别	SCI
语种	英语
资助项目	Science and Technology Program of Guangzhou[202007020008] ; Fundamental Research Funds for the Central Universities[21619334] ; Scientific Research Funds for the Talents and Innovation Foundation of Jinan University
WOS研究方向	Materials Science ; Physics
WOS类目	Materials Science, Coatings & Films ; Physics, Applied
WOS记录号	WOS:000539335900010
出版者	ELSEVIER SCIENCE SA
引用统计	被引频次：5[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/139263
专题	中国科学院金属研究所
通讯作者	Yang, Y. F.; Ren, P.
作者单位	1.Jinan Univ, Inst Adv Wear & Corros Resistant & Funct Mat, Guangzhou 510632, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Lab Corros & Protect, Wencui Rd 62, Shenyang 110016, Peoples R China 3.Northeastern Univ, Corros & Protect Div, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China
推荐引用方式 GB/T 7714	Yang, Y. F.,Ren, P.,Bao, Z. B.,et al. Effect of Pt-rich position on the hot corrosion behavior of NiCoCrAlY coating for a single-crystal superalloy[J]. SURFACE & COATINGS TECHNOLOGY,2020,395:10.
APA	Yang, Y. F.,Ren, P.,Bao, Z. B.,Zhu, S. L.,Wang, F. H.,&Li, W..(2020).Effect of Pt-rich position on the hot corrosion behavior of NiCoCrAlY coating for a single-crystal superalloy.SURFACE & COATINGS TECHNOLOGY,395,10.
MLA	Yang, Y. F.,et al."Effect of Pt-rich position on the hot corrosion behavior of NiCoCrAlY coating for a single-crystal superalloy".SURFACE & COATINGS TECHNOLOGY 395(2020):10.