| Influence of Phosphorus Addition on the Stress Rupture Properties of Direct Aged IN706 Superalloy | |
| Zhang, Sha1; Zhang, Anwen2; Xue, Chaochao2; Jia, Dan2; Zhang, Weiwei2; Wang, Weiyang3; Xin, Xin2; Sun, Wenru2 | |
| 通讯作者 | Zhang, Sha(szhang10b@alum.imr.ac.cn) |
| 2020-08-01 | |
| 发表期刊 | CRYSTALS
 |
| ISSN | 2073-4352 |
| 卷号 | 10期号:8页码:9 |
| 摘要 | This study investigated the influence of phosphorus (P) addition on the stress rupture properties of direct aged IN706 superalloy. The results showed that P slightly improved the stress rupture life of the superalloy when added in the range between 0.002% and 0.008%; however, it significantly reduced the stress rupture life when added in the range between 0.013% and 0.017%. Microstructure characterization indicated that the precipitation of gamma ', gamma '', and eta phases was not significantly affected by the addition of P. Phosphides precipitated in the alloy containing 0.017% P after aging at 980 degrees C for 10 min. Compared to a similar study previously made on IN706 superalloy, it was found that the optimum P concentration in the as-solutioned state for improving the stress rupture properties was not definite. Furthermore, the relationship between the amount of P segregated at the grain boundary and the role of P on the stress rupture properties was discussed. |
| 关键词 | phosphorus direct aging heat treatment stress rupture property grain boundary segregation IN706 alloy |
| 资助者 | Natural Science Foundation of Hunan Province of China ; Science Research Foundation of Hunan Provincial Education Department of China ; Science and Technology Research Foundation of Jiangxi Provincial Education Department of China ; National Natural Science Foundation of China |
| DOI | 10.3390/cryst10080641 |
| 收录类别 | SCI |
| 语种 | 英语 |
| 资助项目 | Natural Science Foundation of Hunan Province of China[2020JJ4645] ; Science Research Foundation of Hunan Provincial Education Department of China[19C0156] ; Science and Technology Research Foundation of Jiangxi Provincial Education Department of China[GJJ170929] ; Science and Technology Research Foundation of Jiangxi Provincial Education Department of China[GJJ180868] ; National Natural Science Foundation of China[11964029] |
| WOS研究方向 | Crystallography ; Materials Science |
| WOS类目 | Crystallography ; Materials Science, Multidisciplinary |
| WOS记录号 | WOS:000567362500001 |
| 出版者 | MDPI |
| 引用统计 | |
| 文献类型 | 期刊论文 |
| 条目标识符 | http://ir.imr.ac.cn/handle/321006/140452 |
| 专题 | 中国科学院金属研究所 |
| 通讯作者 | Zhang, Sha |
| 作者单位 | 1.Changsha Univ, Coll Mech & Elect Engn, Changsha 410022, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 3.Shangrao Normal Univ, Jiangxi Prov Key Lab Polymer Preparat & Proc, Shangrao 334001, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhang, Sha,Zhang, Anwen,Xue, Chaochao,et al. Influence of Phosphorus Addition on the Stress Rupture Properties of Direct Aged IN706 Superalloy[J]. CRYSTALS,2020,10(8):9. |
| APA | Zhang, Sha.,Zhang, Anwen.,Xue, Chaochao.,Jia, Dan.,Zhang, Weiwei.,...&Sun, Wenru.(2020).Influence of Phosphorus Addition on the Stress Rupture Properties of Direct Aged IN706 Superalloy.CRYSTALS,10(8),9. |
| MLA | Zhang, Sha,et al."Influence of Phosphorus Addition on the Stress Rupture Properties of Direct Aged IN706 Superalloy".CRYSTALS 10.8(2020):9. |
| 条目包含的文件 | 条目无相关文件。 | |||||
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论