Effects of annealing treatment on microstructure and tensile behavior of the Mg-Zn-Y-Nd alloy

doi:10.1016/j.jma.2019.07.011

IMR OpenIR

	Effects of annealing treatment on microstructure and tensile behavior of the Mg-Zn-Y-Nd alloy
	Sheng, L. Y.1; Du, B. N.1; Hu, Z. Y.1,4; Qiao, Y. X.2; Xiao, Z. P.2; Wang, B. J.1; Xu, D. K.3; Zheng, Y. F.1; Xi, T. F.1
通讯作者	Sheng, L. Y.(lysheng@yeah.net) ; Du, B. N.(bndu10s@alum.imr.ac.cn)
	2020-09-01
发表期刊	JOURNAL OF MAGNESIUM AND ALLOYS
ISSN	2213-9567
卷号	8 期号:3 页码:601-613
摘要	In the present study, the Mg-4Zn-0.6Y-0.5Nd alloy was hot extruded and annealed at 200 degrees C, 225 degrees C and 250 degrees C for different time to optimize microstructure and mechanical properties. The results exhibit that the dual-size grain structure and linearly distributed secondary phase are the main feature of the as-extruded Mg-Zn-Y-Nd alloy, which can be described as the elongated grain is surrounded by the fine equiaxed grain. Moreover, the as-extruded alloy shows strong {01 (1) over bar0} fiber texture feature, especially for the large elongated grains. The annealing treatment results in static recrystallization, which increases fine equiaxed grains but decreases large elongated grains. In addition, the equiaxed grains formed during the annealing treatment demonstrate relative random orientations, which weaken the {01 (1) over bar0} fiber texture of the alloy. Moreover, during the annealing at 225 degrees C and 250 degrees C, the extension twins begin to form in the alloy and weaken the {01 (1) over bar0} fiber texture of the alloy further. The annealing treatment has little influence on the linearly distributed secondary phase but promotes the coarsening of small precipitates at 250 degrees C. The annealing treatment could increase the yield and ultimate strength, but the elongation decreases, especially at higher temperature. Such a variation can be ascribed to the evolution of texture, grain structure, twinning and precipitation during the annealing treatment. (c) 2020 Published by Elsevier B.V. on behalf of Chongqing University.
关键词	Annealing treatment Mg-Zn-Y-Nd alloy Microstructure Tensile property
资助者	Natural Science Foundation of Guangdong Province, China ; Shenzhen Basic Research Project
DOI	10.1016/j.jma.2019.07.011
收录类别	SCI
语种	英语
资助项目	Natural Science Foundation of Guangdong Province, China[2018A030313950] ; Shenzhen Basic Research Project[JCYJ20170815153143221] ; Shenzhen Basic Research Project[JCYJ20170815153210359] ; Shenzhen Basic Research Project[JCYJ20170306141749970]
WOS研究方向	Metallurgy & Metallurgical Engineering
WOS类目	Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000571358200004
出版者	KEAI PUBLISHING LTD
引用统计	被引频次：66[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/140700
专题	中国科学院金属研究所
通讯作者	Sheng, L. Y.; Du, B. N.
作者单位	1.Peking Univ, Shenzhen Inst, Shenzhen 518057, Peoples R China 2.Jiangsu Univ Sci & Technol, Zhenjiang 212003, Jiangsu, Peoples R China 3.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 4.Shenzhen Yezhan Elect Co Ltd, Shenzhen 518110, Peoples R China
推荐引用方式 GB/T 7714	Sheng, L. Y.,Du, B. N.,Hu, Z. Y.,et al. Effects of annealing treatment on microstructure and tensile behavior of the Mg-Zn-Y-Nd alloy[J]. JOURNAL OF MAGNESIUM AND ALLOYS,2020,8(3):601-613.
APA	Sheng, L. Y..,Du, B. N..,Hu, Z. Y..,Qiao, Y. X..,Xiao, Z. P..,...&Xi, T. F..(2020).Effects of annealing treatment on microstructure and tensile behavior of the Mg-Zn-Y-Nd alloy.JOURNAL OF MAGNESIUM AND ALLOYS,8(3),601-613.
MLA	Sheng, L. Y.,et al."Effects of annealing treatment on microstructure and tensile behavior of the Mg-Zn-Y-Nd alloy".JOURNAL OF MAGNESIUM AND ALLOYS 8.3(2020):601-613.