Cross-Section Effect of Ni-Cr-Mo-B Ultra-Heavy Steel Plate for Offshore Platform

doi:10.11900/0412.1961.2020.00007

IMR OpenIR

	Cross-Section Effect of Ni-Cr-Mo-B Ultra-Heavy Steel Plate for Offshore Platform
	Zhang Shouqing 1,2; Hu Xiaofeng 1; Du Yubin 1,2; Jiang Haichang 1; Pang Huiyong 3; Rong Lijian 1
通讯作者	Rong Lijian(ljrong@imr.ac.cn)
	2020-09-01
发表期刊	ACTA METALLURGICA SINICA
ISSN	0412-1961
卷号	56 期号:9 页码:1227-1238
摘要	With the increasing demand and exploitation depth for offshore oil and gas, offshore platforms are becoming larger and the performance requirements and size for offshore platform of ultra-heavy plates are also increasing. Due to the large plate thickness and the limitation of manufacturing techniques, inhomogeneous microstructures and mechanical properties along thickness direction are great challenges for offshore platform of ultra-heavy plates. In this work, variation of microstructure and its effect on mechanical properties for the 117 mm-thick Ni-Cr-Mo-B industrial ultra-heavy plate were investigated by means of OM, SEM, TEM and EBSD observation, in combination with the tensile and impact toughness test. The results show that yield strength reduces gradually from the surface (798 MPa) to the center (718 MPa) and elongation almost keeps constant around 20.0%similar to 22.0% for the 117 mm-thick plate. It is noted that impact energy at -60 degrees C increases first from 35 J at the surface and reaches its peak 160 J at the depth of 1/8T (T-thickness of plate), and then drops to the minimum about 20 J at the center, which suggests that impact energy curve along the whole section varies sharply and exhibits like letter 'M'. Lath width, boundary carbide size and intragranular carbide size are all gradually increasing from the surface to the center, i. e., from 198.7 nm to 500.6 nm, 130.6 nm to 226.6 nm, 45.8 nm to 106.2 nm, respectively, and there are also some blocky areas at the center, all those indicate that refinement strengthening and precipitation strengthening would decrease, as well as the gradual decrease of yield strength. Also, from the surface to the center, effective grain size (EGS) decreases first and then increases. The surface and the center have larger EGS (2.2 mu m and 2.7 mu m, respectively), which indicates that they have weaker resistance to cleavage crack and exhibit lower impact energy. However, the 1/8T position has smaller EGS (1.7 mu m) while obtains higher impact energy.
关键词	Ni-Cr-Mo-B steel ultra-heavy plate cross-section effect impact energy effective grain size
资助者	National Key Research and Development Program of China ; Liaoning Revitalization Talents Program ; Major Science and Technology Projects of Construction Corps
DOI	10.11900/0412.1961.2020.00007
收录类别	SCI
语种	英语
资助项目	National Key Research and Development Program of China[2016YFB0300601] ; Liaoning Revitalization Talents Program ; Major Science and Technology Projects of Construction Corps
WOS研究方向	Metallurgy & Metallurgical Engineering
WOS类目	Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000576758600005
出版者	SCIENCE PRESS
引用统计	被引频次：10[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/140803
专题	中国科学院金属研究所
通讯作者	Rong Lijian
作者单位	1.Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China 3.Wuyang Iron & Steel Co Ltd, Pingdingshan 462500, Peoples R China
推荐引用方式 GB/T 7714	Zhang Shouqing,Hu Xiaofeng,Du Yubin,et al. Cross-Section Effect of Ni-Cr-Mo-B Ultra-Heavy Steel Plate for Offshore Platform[J]. ACTA METALLURGICA SINICA,2020,56(9):1227-1238.
APA	Zhang Shouqing,Hu Xiaofeng,Du Yubin,Jiang Haichang,Pang Huiyong,&Rong Lijian.(2020).Cross-Section Effect of Ni-Cr-Mo-B Ultra-Heavy Steel Plate for Offshore Platform.ACTA METALLURGICA SINICA,56(9),1227-1238.
MLA	Zhang Shouqing,et al."Cross-Section Effect of Ni-Cr-Mo-B Ultra-Heavy Steel Plate for Offshore Platform".ACTA METALLURGICA SINICA 56.9(2020):1227-1238.