MICROSEGREGATION OF SOLUTE ELEMENTS IN SOLIDIFYING MUSHY ZONE OF STEEL AND ITS EFFECT ON LONGITUDINAL SURFACE CRACKS OF CONTINUOUS CASTING STRAND
Alternative TitleMICROSEGREGATION OF SOLUTE ELEMENTS IN SOLIDIFYING MUSHY ZONE OF STEEL AND ITS EFFECT ON LONGITUDINAL SURFACE CRACKS OF CONTINUOUS CASTING STRAND
Cai Zhaozhen; Zhu Miaoyong
2009
Source PublicationACTA METALLURGICA SINICA
ISSN0412-1961
Volume45Issue:8Pages:949-955
AbstractThe solidification of molten steel in continuous casting mold is a complicated non-equilibrium process with high cooling rate of 10-100 degrees C/s. At such a cooling rate, the segregation of the solute elements such as C, Si, Mn, P and S in brittle temperature range (Delta theta(B)) will vary with their initial contents and influence on the thermal strain significantly which could greatly increase the incidence of surface defects of strand. In this paper, a microsegregation model of solute elements in mushy zone with delta/gamma transformation during solidification was established based on the regular hexagon transverse cross section of dendrite shape proposed by Ueshima by finite difference method under the non-equilibrium solidification condition at 10 degrees C/s of cooling rate and the brittle temperature range Delta theta(B) was determined. The distribution characteristics of solute elements and the effect of their segregations on Delta theta(B) and thermal strain were investigated. The results show that both P and S are the most serious segregation elements in final stage of solidification and affect On Delta theta(B) significantly together with carbon content in molten steel. The mechanism that increasing contents of P and S may increase the probability of longitudinal surface crack for continuous casting strand was presented by calculating the change law of thermal strain with carbon content under different of P and S contents.
KeywordDELTA-GAMMA-TRANSFORMATION CARBON CONTENT SOLIDIFICATION BEHAVIOR MELT continuous casting microsegregation longitudinal surface cracks brittle temperature range thermal strain
Indexed ByCSCD
Language英语
Funding Project[New century Excellent Talents in University]
CSCD IDCSCD:3752450
Citation statistics
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/141966
Collection中国科学院金属研究所
Affiliation中国科学院金属研究所
Recommended Citation
GB/T 7714
Cai Zhaozhen,Zhu Miaoyong. MICROSEGREGATION OF SOLUTE ELEMENTS IN SOLIDIFYING MUSHY ZONE OF STEEL AND ITS EFFECT ON LONGITUDINAL SURFACE CRACKS OF CONTINUOUS CASTING STRAND[J]. ACTA METALLURGICA SINICA,2009,45(8):949-955.
APA Cai Zhaozhen,&Zhu Miaoyong.(2009).MICROSEGREGATION OF SOLUTE ELEMENTS IN SOLIDIFYING MUSHY ZONE OF STEEL AND ITS EFFECT ON LONGITUDINAL SURFACE CRACKS OF CONTINUOUS CASTING STRAND.ACTA METALLURGICA SINICA,45(8),949-955.
MLA Cai Zhaozhen,et al."MICROSEGREGATION OF SOLUTE ELEMENTS IN SOLIDIFYING MUSHY ZONE OF STEEL AND ITS EFFECT ON LONGITUDINAL SURFACE CRACKS OF CONTINUOUS CASTING STRAND".ACTA METALLURGICA SINICA 45.8(2009):949-955.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Cai Zhaozhen]'s Articles
[Zhu Miaoyong]'s Articles
Baidu academic
Similar articles in Baidu academic
[Cai Zhaozhen]'s Articles
[Zhu Miaoyong]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Cai Zhaozhen]'s Articles
[Zhu Miaoyong]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.