Effect of Aging Heat Treatment on Microstructure and Properties of Laser Deposition Repaired GH738 Alloy

IMR OpenIR

	Effect of Aging Heat Treatment on Microstructure and Properties of Laser Deposition Repaired GH738 Alloy
	Bian Hongyou; Zhai Quanxing; Qu Shen; Yang Guang; Wang Wei; Wang Wei
	2019
发表期刊	RARE METAL MATERIALS AND ENGINEERING
ISSN	1002-185X
卷号	48 期号:1 页码:317-322
摘要	The effects of bipolar aging heat treatment on the microstructure and mechanical properties of GH738 alloy repaired by laser deposition were studied. The results show that the microstructure of repair area presents typical characteristics of the epitaxial growth of columnar crystals and the dendrite spacing is about 10 gm. After the aging treatment, the repair area begins to grow and merge. The results of SEM analysis show that there is no gamma' at the as-deposited sample, and the cubic MC type carbide is formed at the interdendritic, and the M23C6 type carbide at the dendrite arm. After the aging treatment, gamma' phase precipitates at the repair area whose average size is 37 nm, and the carbide precipitates in the grain boundary with the discontinued character when the temperature of the stabilization step is 820 degrees C. With the increase of the stabilization temperature, the size of the gamma' and carbide increases. When the temperature is 840 degrees C, the average size of the gamma' is about 76 nm, and the carbide is precipitated in the form of necklace. With increasing the temperature of the stabilization step to 860 degrees C, the average size of the gamma' does not increase obviously, and part of the gamma' is obviously coarsened and the size reaches to 150 nm; meanwhile the carbides at the grain boundaries begin to be closed. The results of mechanical property show that the tensile strength of the sample increases obviously after aging treatment, and with the increase of the temperature, the tensile strength increases first and then decreases, and the elongation decreases continuously.
关键词	PRECIPITATION SUPERALLOY laser deposition repair GH738 alloy heat treatment microstructure mechanical properties
收录类别	CSCD
语种	英语
CSCD记录号	CSCD:6412137
引用统计	被引频次：7[CSCD] [CSCD记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/143199
专题	中国科学院金属研究所
作者单位	中国科学院金属研究所
推荐引用方式 GB/T 7714	Bian Hongyou,Zhai Quanxing,Qu Shen,et al. Effect of Aging Heat Treatment on Microstructure and Properties of Laser Deposition Repaired GH738 Alloy[J]. RARE METAL MATERIALS AND ENGINEERING,2019,48(1):317-322.
APA	Bian Hongyou,Zhai Quanxing,Qu Shen,Yang Guang,Wang Wei,&Wang Wei.(2019).Effect of Aging Heat Treatment on Microstructure and Properties of Laser Deposition Repaired GH738 Alloy.RARE METAL MATERIALS AND ENGINEERING,48(1),317-322.
MLA	Bian Hongyou,et al."Effect of Aging Heat Treatment on Microstructure and Properties of Laser Deposition Repaired GH738 Alloy".RARE METAL MATERIALS AND ENGINEERING 48.1(2019):317-322.