用优化的Na2SiO3电解液制备的镁合金陶瓷膜的防护性能
Alternative TitleCORROSION PERFORMANCE OF CERAMIC FILMS FABRICATED ON AZ91D MAGNESIUM ALLOY BY PLASMA ELETROLYTIC OXIDATION IN AN OPTIMIZED Na2SiO3 CONTAINING SOLUTION
张慧霞; 张伟; 李月洁; 杜克勤; 严川伟
2008
Source Publication腐蚀科学与防护技术
ISSN1002-6495
Volume20.0Issue:004Pages:268-271
Abstract优化镁合金微弧氧化常用的Na2SiO3电解液并制备了白色陶瓷质微弧氧化膜,采用动电位极化曲线和电化学交流阻抗(EIS)等方法研究其防护性能.结果表明,与常用的Na2SiO3电解液制备的试样相比,优化的Na2SiO3电解液所制备试样的自腐蚀电流降低了3个数量级,并表现出较高的阻抗值;在3.5%NaCl溶液中浸泡发生点蚀的时间从24 h延长到240 h.SEM和XRD分析结果表明,在优化的Na2SiO3电解液中制备的AZ91D的陶瓷膜层孔隙减少,孔径也较小,且增加了低溶解度的Mg5F2(SiO4)2相和起钝化作用的MgAl2O4相.
Other AbstractPlasma electrolytic oxidation of AZ91D magnesium alloy was studied in an optimized solution mainly containing Na2SiO3. The microstructure, phase constituents and elemental distribution of ceramic films were investigated by using scanning electron microscopy (SEM) and X-ray diffraction (XRD). The corrosion resistance of the magnesium alloy with ceramic films were evaluated by potentiodynamic polarization curves and electrochemical impedance spectroscopy (EIS). The results indicated that Icorr of the magnesium alloy oxidized in the optimized solution was decreased by three orders of magnitude compared with that oxidized in the conventional solution. The polarization resistance of the magnesium alloy oxidized in the optimized solution was higher than that oxidized in the conventional solution, and the time for appearance of obvious corrosion pits during immersion in 3.5% NaCl solution was increased from 24 h for the sample oxidized in the conventional solution to 240 h for that oxidized in the optimized solution. The better corrosion resistance of the magnesium alloy oxidized in the optimized solution results from fewer defects, fewer pores, as well as higher content of the phase of Mg5 F2 (SiO4 )2 with lower dissolubility and the MgAl2O4 with better passivity in the oxide film.
Keyword镁合金 微弧氧化 防护性能 Na2SiO3电解液
Indexed ByCSCD
Language中文
CSCD IDCSCD:3342652
Citation statistics
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/144021
Collection中国科学院金属研究所
Affiliation中国科学院金属研究所
Recommended Citation
GB/T 7714
张慧霞,张伟,李月洁,等. 用优化的Na2SiO3电解液制备的镁合金陶瓷膜的防护性能[J]. 腐蚀科学与防护技术,2008,20.0(004):268-271.
APA 张慧霞,张伟,李月洁,杜克勤,&严川伟.(2008).用优化的Na2SiO3电解液制备的镁合金陶瓷膜的防护性能.腐蚀科学与防护技术,20.0(004),268-271.
MLA 张慧霞,et al."用优化的Na2SiO3电解液制备的镁合金陶瓷膜的防护性能".腐蚀科学与防护技术 20.0.004(2008):268-271.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[张慧霞]'s Articles
[张伟]'s Articles
[李月洁]'s Articles
Baidu academic
Similar articles in Baidu academic
[张慧霞]'s Articles
[张伟]'s Articles
[李月洁]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[张慧霞]'s Articles
[张伟]'s Articles
[李月洁]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.