EFFECTS OF RAPID HEATING CONTINUOUS ANNEALING ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF ULTRA HIGH-STRENGTH TRIP-AIDED STEEL

IMR OpenIR

	EFFECTS OF RAPID HEATING CONTINUOUS ANNEALING ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF ULTRA HIGH-STRENGTH TRIP-AIDED STEEL
其他题名	EFFECTS OF RAPID HEATING CONTINUOUS ANNEAL ING ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF ULTRA HIGH-STRENGTH TRIP-AIDED STEEL
	Xu Yunbo 1; Hou Xiaoying 1; Wang Yeqin 2; Wu Di 1
	2012
发表期刊	ACTA METALLURGICA SINICA
ISSN	0412-1961
卷号	48 期号:2 页码:176-182
摘要	The effects of rapid heating continuous annealing on microstructure and mechanical properties of ultra-high strength and low silicon TRIP steel containing phosphorus and vanadium were investigated. The results show that the yield and tensile strengths are increased with increasing intercritical annealing temperature during rapid continuous annealing. However, the intercritical annealing temperature can not increase blindly to ensure its excellent combined mechanical properties. When the heating rate is 80 degrees C /s and intercritical annealing temperature is 880 degrees C the retained austenite not only contains fine blocky structure, but also a large amount of interlath retained austenite films A great amount of V(C, N) precipitates exists within ferritic matrix, and the sizes of most of the precipates are in the range from 4 to 9 nm. The tested steel has excellent mechanical properties: R-m= 1010 MPa, R-P0.2=690 MPa, delta=23.6%, n=0.27, r=1.17, the product of strength and ductility (R-m x delta) is 23836 MPa.%. If the intercritical annealing temperature is too high or too low, the comprehensive mechanical properties will be deteriorated since the volume fraction of retained austenite reduces, morphology changes and its size increase.
关键词	RETAINED AUSTENITE GRAIN-REFINEMENT SI TRANSFORMATION NB PHOSPHORUS ALUMINUM SHEET AL TRIP steel containing vanadiun rapid heating continuous annealing mechanical property retained austenite
收录类别	CSCD
语种	英语
CSCD记录号	CSCD:4521951
引用统计	被引频次：12[CSCD] [CSCD记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/144933
专题	中国科学院金属研究所
作者单位	1.中国科学院金属研究所 2.Laiwu Iron & Steel Grp Co Ltd, Laiwu 271104, Peoples R China
推荐引用方式 GB/T 7714	Xu Yunbo,Hou Xiaoying,Wang Yeqin,et al. EFFECTS OF RAPID HEATING CONTINUOUS ANNEALING ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF ULTRA HIGH-STRENGTH TRIP-AIDED STEEL[J]. ACTA METALLURGICA SINICA,2012,48(2):176-182.
APA	Xu Yunbo,Hou Xiaoying,Wang Yeqin,&Wu Di.(2012).EFFECTS OF RAPID HEATING CONTINUOUS ANNEALING ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF ULTRA HIGH-STRENGTH TRIP-AIDED STEEL.ACTA METALLURGICA SINICA,48(2),176-182.
MLA	Xu Yunbo,et al."EFFECTS OF RAPID HEATING CONTINUOUS ANNEALING ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF ULTRA HIGH-STRENGTH TRIP-AIDED STEEL".ACTA METALLURGICA SINICA 48.2(2012):176-182.