Effect of Cooling Rate on Microstructure and Mechanical Properties of K465 Superalloy

IMR OpenIR

	Effect of Cooling Rate on Microstructure and Mechanical Properties of K465 Superalloy
其他题名	Effect of Cooling Rate on Microstructure and Mechanical Properties of K465 Superalloy
	Pei Zhongye 1; Han Wei 2; Zhao Gang 2; Chen Xingfu 2; Li Juntao 2; Tian Yanwen 1
	2009
发表期刊	JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL
ISSN	1006-706X
卷号	16 期号:6 页码:70-74
摘要	K465 superalloy, as a material for production of turbine nozzle, shows high mechanical properties as well as microstructure stability under critical and severe service conditions. The appropriate microstructure and strength of this alloy can be obtained by solid solution strengthening mechanism. Heat treatment parameters such as time and temperature of homogenization, partial solution and aging temperatures, and cooling rate from solid solution temperature. affect the microstructure of the alloy. Among these parameters, cooling rate from solid solution temperature is the most effective. Therefore, the effect of cooling rate on microstructure and mechanical properties (tensile and stress properties) was investigated. For this purpose, three different cooling rates were applied to the cast K465 specimens subjected to solution treatment at 1 483 K for 4 h. Microstructures of the specimens then were studied using optical and electron microscopy. Also, tensile tests were performed at room temperature and stress rupture tests were performed under the condition of 1 248. K and 230 MPa. It was found that with increasing the cooling rate, the size of the gamma' precipitates decreases and the mechanical properties of specimens increases. Also, it was found that the shape and volume fraction of primary gamma' particles are largely influenced by the cooling rate after solution treatment at 1 483 K for 4 h.
其他摘要	K465 superalloy, as a material for production of turbine nozzle, shows high mechanical properties as well as microstructure stability under critical and severe service conditions. The appropriate microstructure and strength of this alloy can be obtained by solid solution strengthening mechanism. Heat treatment parameters such as time and temperature of homogenization, partial solution and aging temperatures, and cooling rate from solid solution temper-ature affect the microstructure of the alloy. Among these parameters, cooling rate from solid solution temperature is the most effective. Therefore, the effect of cooling rate on microstructure and mechanical properties (tensile and stress properties)was investigated. For this purpose, three different cooling rates were applied to the cast K465 specimens subjected to solution treatment at 1483 K for 4 h. Microstructures of the specimens then were studied u-sing optical and electron microscopy. Also, tensile tests were performed at room temperature and stress rupture tests were performed under the condition of 1248 K and 230 MPa. It was found that with increasing the cooling rate, the size of the γ' precipitates decreases and the mechanical properties of specimens increases. Also, it was found that the shape and volume fraction of primary γ' particles are largely influenced by the cooling rate after solution treatment at 1483 K for4 h.
关键词	NICKEL-BASE SUPERALLOY POWDER-METALLURGY SUPERALLOY HEAT-TREATMENT PRECIPITATION CREEP cast superalloy solution heat treatment cooling rate microstructure mechanical property
收录类别	CSCD
语种	英语
CSCD记录号	CSCD:3734641
引用统计
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/145806
专题	中国科学院金属研究所
作者单位	1.中国科学院金属研究所 2.Cent Iron & Steel Res Institute, High Temp Mat Res Div, Beijing 100081, Peoples R China
推荐引用方式 GB/T 7714	Pei Zhongye,Han Wei,Zhao Gang,et al. Effect of Cooling Rate on Microstructure and Mechanical Properties of K465 Superalloy[J]. JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL,2009,16(6):70-74.
APA	Pei Zhongye,Han Wei,Zhao Gang,Chen Xingfu,Li Juntao,&Tian Yanwen.(2009).Effect of Cooling Rate on Microstructure and Mechanical Properties of K465 Superalloy.JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL,16(6),70-74.
MLA	Pei Zhongye,et al."Effect of Cooling Rate on Microstructure and Mechanical Properties of K465 Superalloy".JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL 16.6(2009):70-74.