| 镁合金应力腐蚀开裂行为研究进展 | |
| 其他题名 | Research Progress on Stress Corrosion Cracking Behavior of Magnesium Alloys |
| 王保杰1; 栾吉瑜1; 王士栋2; 许道奎2 | |
| 2019 | |
| 发表期刊 | 中国腐蚀与防护学报
 |
| ISSN | 1005-4537 |
| 卷号 | 000期号:002页码:89-95 |
| 摘要 | 系统总结了镁合金的应力腐蚀开裂行为及其微观失效机制的研究进展,重点介绍了阳极溶解、机械载荷、氢脆效应等对裂纹开裂模式的影响和作用规律,以及提高镁合金抗应力腐蚀开裂能力的处理方法及其作用机制;指出目前研究中存在的问题,并提出未来的研究重点和发展方向。 |
| 其他摘要 | In this paper,the stress corrosion cracking(SCC)behavior of Mg-alloys and the relevant failure mechanism were systematically summarized.Moreover,the effect of anodic dissolution,mechanical loading and hydrogen embrittlement on the SCC cracking modes was described.The measures for improving the SCC resistance of Mg-alloys were also introduced.Finally,the existing problems in the current study,the research emphasis and direction in the future are also pointed out. |
| 关键词 | 镁合金 应力腐蚀开裂 局部腐蚀 氢致开裂 腐蚀机制 |
| 收录类别 | CSCD |
| 语种 | 中文 |
| CSCD记录号 | CSCD:6491509 |
| 引用统计 | |
| 文献类型 | 期刊论文 |
| 条目标识符 | http://ir.imr.ac.cn/handle/321006/147782 |
| 专题 | 中国科学院金属研究所 |
| 作者单位 | 1.沈阳理工大学 2.中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | 王保杰,栾吉瑜,王士栋,等. 镁合金应力腐蚀开裂行为研究进展[J]. 中国腐蚀与防护学报,2019,000(002):89-95. |
| APA | 王保杰,栾吉瑜,王士栋,&许道奎.(2019).镁合金应力腐蚀开裂行为研究进展.中国腐蚀与防护学报,000(002),89-95. |
| MLA | 王保杰,et al."镁合金应力腐蚀开裂行为研究进展".中国腐蚀与防护学报 000.002(2019):89-95. |
| 条目包含的文件 | 条目无相关文件。 | |||||
| 个性服务 |
| 推荐该条目 |
| 保存到收藏夹 |
| 查看访问统计 |
| 导出为Endnote文件 |
| 谷歌学术 |
| 谷歌学术中相似的文章 |
| [王保杰]的文章 |
| [栾吉瑜]的文章 |
| [王士栋]的文章 |
| 百度学术 |
| 百度学术中相似的文章 |
| [王保杰]的文章 |
| [栾吉瑜]的文章 |
| [王士栋]的文章 |
| 必应学术 |
| 必应学术中相似的文章 |
| [王保杰]的文章 |
| [栾吉瑜]的文章 |
| [王士栋]的文章 |
| 相关权益政策 |
| 暂无数据 |
| 收藏/分享 |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论