激光脉冲法研究半透明PI/SiO2薄膜的热扩散率
Alternative TitleThermal Diffusivity Research of PI/SiO2 Films by Laser Flash Method
陈新贵; 郭敬东; 王宝全; 何冠虎
2009
Source Publication高分子材料科学与工程
ISSN1000-7555
Volume25.0Issue:004Pages:109-111
Abstract激光脉冲法在应用于测量对实验探测波段红外线半透明的材料热扩散率时遇到了困难。文中提出了新的解决办法:即通过对理论探测曲线进行分析,并通过在实际探测曲线上的升温幅度和特征点计算得到了热扩散率,成功地解决了这一难题。在-73℃~290℃的范围内获得了对激光和红外线都是半透明的聚酰亚胺(PI)薄膜的热扩散率,并研究了室温下PI/SiO2复合材料的热扩散率随SiO2含量的变化规律。
Other AbstractLaser flash method was succeeded in thermal diffusivity t, and with the heat capacity and density, the thermal conductivity can be calculated out. But it is difficult to apply this method in the thermal diffusivity measurement of semitransparent materials, especially for those materials which were semitransparent both in the infra-red wave length of laser beam and detector. In this paper, a new method has been made up to solve this problem. The diffusivity of polyimide (PI) film was measured in the temperature range of - 73 ℃ -290 ℃ and the thermal diffusivity of PI/SiO2 composite films with different content of SiO2 were researched also.
Keyword激光脉冲法 半透明材料 热扩散率 PI/SiO2复合材料
Indexed ByCSCD
Language中文
CSCD IDCSCD:3583015
Citation statistics
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/148443
Collection中国科学院金属研究所
Affiliation中国科学院金属研究所
Recommended Citation
GB/T 7714
陈新贵,郭敬东,王宝全,等. 激光脉冲法研究半透明PI/SiO2薄膜的热扩散率[J]. 高分子材料科学与工程,2009,25.0(004):109-111.
APA 陈新贵,郭敬东,王宝全,&何冠虎.(2009).激光脉冲法研究半透明PI/SiO2薄膜的热扩散率.高分子材料科学与工程,25.0(004),109-111.
MLA 陈新贵,et al."激光脉冲法研究半透明PI/SiO2薄膜的热扩散率".高分子材料科学与工程 25.0.004(2009):109-111.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[陈新贵]'s Articles
[郭敬东]'s Articles
[王宝全]'s Articles
Baidu academic
Similar articles in Baidu academic
[陈新贵]'s Articles
[郭敬东]'s Articles
[王宝全]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[陈新贵]'s Articles
[郭敬东]'s Articles
[王宝全]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.