5083铝合金表面单致密微弧氧化膜的制备及其性能研究
Alternative TitlePreparation and Properties of Micro-arc Oxide Film with Single Dense Layer on Surface of 5083 Aluminum Alloy
曹京宜1; 方志刚1; 陈晋辉2; 陈志雄2; 殷文昌1; 杨延格1; 张伟3
2020
Source Publication中国腐蚀与防护学报
ISSN1005-4537
Volume40.0Issue:003Pages:251-258
Abstract采用响应曲面法对微弧氧化电解液体系进行了优化,并在5083铝合金表面进行了单致密微弧氧化涂层的制备。通过扫描电镜、X射线衍射仪、显微硬度计和极化曲线对铝合金微弧氧化膜的微观组织、显微硬度和耐蚀性进行了研究。结果表明:随着微弧氧化膜层厚度从30μm增加到90μm,烧结颗粒的尺寸从约为10μm增加到约为50μm,致密层由最初的20μm增加到70μm,陶瓷膜层中α-Al2O3的比例明显增加,涂层的硬度由900 HV提高到1500 HV。依据极化曲线和盐雾实验结果发现:随着微弧氧化时间的增加,微弧氧化膜的自腐蚀电流密度逐渐降低,钝化能力逐渐增强,膜层的耐腐蚀性能大幅度提高。
Other AbstractMarine Al-alloy 5083 owns low density,good weldability and high hardness,but it is easily suffered from pitting corrosion in sea water due to the effect of Cl-.Micro-arc oxidation(MAO)is an effective way to improve the corrosion resistance of Al-alloy.In the present study the electrolyte formula was optimized via response surface methodology so that to acquire a novel MAO coating on Al-alloy 5083,which composed of merely a dense layer.The prepare MAO coating was then characterized by scanning electron microscopy(SEM),X-ray diffraction(XRD),micro-hardness meter and dynamic polarization technology in terms of microstructure,micro-hardness and corrosion resistance.Results showed that in comparison with the coating prepared with the ordinary electrolyte,the thickness of the MAO coating increases from 30μm to 90μm,size of the sintered particles on MAO coating grown from 10μm to 50μm,and the thickness of the dense layer increased from 20μm to 70μm,accompanied by the increase of the percentage ofα-Al2O3 in the MAO coating as well.The hardness of the polished MAO coating increased from 900 HV to 1500 HV.Polarization curve and salt frog test results also found that with the increasing of micro-arc oxidation time,the corrosion current density of MAO coating was gradually decreased,while its passivation ability was enhanced.Therefore,corrosion resistance of Al-alloy 5083 was increased substantially in the presence of the MAO coating composed merely of a thick dense layer.
Keyword铝合金 微弧氧化 单致密层 耐蚀性
Indexed ByCSCD
Language中文
CSCD IDCSCD:6741209
Citation statistics
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/148450
Collection中国科学院金属研究所
Affiliation1.中国人民解放军92228部队
2.福建龙溪轴承股份有限公司
3.中国科学院金属研究所
Recommended Citation
GB/T 7714
曹京宜,方志刚,陈晋辉,等. 5083铝合金表面单致密微弧氧化膜的制备及其性能研究[J]. 中国腐蚀与防护学报,2020,40.0(003):251-258.
APA 曹京宜.,方志刚.,陈晋辉.,陈志雄.,殷文昌.,...&张伟.(2020).5083铝合金表面单致密微弧氧化膜的制备及其性能研究.中国腐蚀与防护学报,40.0(003),251-258.
MLA 曹京宜,et al."5083铝合金表面单致密微弧氧化膜的制备及其性能研究".中国腐蚀与防护学报 40.0.003(2020):251-258.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[曹京宜]'s Articles
[方志刚]'s Articles
[陈晋辉]'s Articles
Baidu academic
Similar articles in Baidu academic
[曹京宜]'s Articles
[方志刚]'s Articles
[陈晋辉]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[曹京宜]'s Articles
[方志刚]'s Articles
[陈晋辉]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.