Ti-48Al-8Cr-2Ag纳米晶涂层对TiAlNb合金腐蚀行为的影响

IMR OpenIR

	Ti-48Al-8Cr-2Ag纳米晶涂层对TiAlNb合金腐蚀行为的影响
其他题名	Effect of Ti-48Al-8Cr-2Ag coating on the cast TiAlNb alloy in the presence of NaCl and water vapor
	席艳君 1; 王福会 2
	2006
发表期刊	材料研究学报
ISSN	1005-3093
卷号	20.0 期号:1.0 页码:37-42
摘要	研究了磁控溅射的Ti-48Al-8Cr-2Ag（原子数分数，％）纳米晶涂层对Ti-46．5Al-5Nb合金腐蚀行为的影响．结果表明，在600～700℃盐水蒸气的协同作用下，TiAlCrAg涂层使TiAlNb合金腐蚀速率降低．Nb是TiAlNb合金在700℃盐水蒸气协同作用下生成致密TiO2膜的主要原因．氯化物侵蚀α2相，使TiAlNb合金在盐和水蒸气综合作用下加速腐蚀，TiAlCrAg涂层中较少的α2相以及Laves相中较高的Cr含量是腐蚀速率降低的主要原因．
其他摘要	Ti-48Al-8Cr-2Ag （atomic fraction, %） coating on the cast TiAlNb alloy was produced by magnetron-sputter deposition. The effect of Ti-48Al-8Cr-2Ag nanocrystalline coating on corrosion behavior of cast TiAlNb alloy has been investigated in the presence of NaCl and water vapor at 500～700℃. The results show that corrosion is severely speeded up when the atmosphere contains NaCl and water vapor. With the increase of the temperature, corrosion speed increases. The dense TiO2 scale forms on the surface of the TiAINb alloy in the presence of NaCl and water vapor at 700℃ due to the effect of the Nb element. The TiAlNb alloy exhibits higher corrosion rate than the alloy with TiAlCrAg coating because chloride intruded into α2 phase of the TiAlNb alloy. In addition, higher Cr content in Laves phase is one of the reasons of the lower corrosion rate of the coating.
关键词	材料失效与保护水蒸气与盐协同作用 TiAlCrAg纳米晶涂层腐蚀
收录类别	CSCD
语种	中文
CSCD记录号	CSCD:2308806
引用统计
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/150906
专题	中国科学院金属研究所
作者单位	1.中原工学院 2.中国科学院金属研究所
推荐引用方式 GB/T 7714	席艳君,王福会. Ti-48Al-8Cr-2Ag纳米晶涂层对TiAlNb合金腐蚀行为的影响[J]. 材料研究学报,2006,20.0(1.0):37-42.
APA	席艳君,&王福会.(2006).Ti-48Al-8Cr-2Ag纳米晶涂层对TiAlNb合金腐蚀行为的影响.材料研究学报,20.0(1.0),37-42.
MLA	席艳君,et al."Ti-48Al-8Cr-2Ag纳米晶涂层对TiAlNb合金腐蚀行为的影响".材料研究学报 20.0.1.0(2006):37-42.