| Synthesis, characterization and electromagnetic studies on nanocrystalline Co0.5Zn0.5Fe2O4 synthesized by polyacrylamide gel | |
| Alternative Title | Synthesis, Characterization and Electromagnetic Studies on Nanocrystalline Co0.5Zn0.5Fe2O4 Synthesized by Polyacrylamide Gel |
| Ma Ruiting; Tian Yanwen; Zhao Haitao; Zhang Gang; Zhao Hui | |
| 2008 | |
| Source Publication | JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
 |
| ISSN | 1005-0302 |
| Volume | 24Issue:4Pages:628-632 |
| Abstract | Nanocrystalline Co0.5Zn0.5Fe2O4 ferrite was synthesized by polyacrylamide gel method. The electromagnetic and microwave absorption properties of the ferrite were investigated. The results indicated that calcining temperature of the ferrite had a significant influence on the effective properties of the ferrite. When the calcining temperature was 500, 600 and 700 degrees C, the average size of particles was 10, 30 and 80 nm, respectively. The dielectric loss (epsilon '') and magnetic loss (u '') of the ferrite was around 0.65 and 0.29 at 8.2 GHz, respectively. Microwave absorption properties of the ferrites were simultaneously influenced due to the strong correlation between reflection loss and electromagnetic parameters of the ferrite. |
| Other Abstract | Nanocrystalline Co0.5Zn0.5Fe2O4 ferrite was synthesized by polyacrylamide gel method. The electromagnetic and microwave absorption properties of the ferrite were investigated. The results indicated that calcining temperature of the ferrite had a significant influence on the effective properties of the ferrite. When the calcining temperature was 500,600 and 700℃, the average size of particles was 10, 30 and 80 nm, respectively. The dielectric loss (ε") and magnetic loss (u") of the ferrite was around 0.65 and 0.29 at 8.2 GHz, respectively. Microwave absorption properties of the ferrites were simultaneously influenced due to the strong correlation between reflection loss and electromagnetic parameters of the ferrite. |
| Keyword | ZN FERRITE POWDERS MAGNETIC-PROPERTIES ZINC FERRITES NIZN FERRITE PARTICLES polyacrylamide gel nanocrystalline Co0.5Zn0.5Fe2O4 electromagnetic properties |
| Indexed By | CSCD |
| Language | 英语 |
| CSCD ID | CSCD:3384123 |
| Citation statistics | |
| Document Type | 期刊论文 |
| Identifier | http://ir.imr.ac.cn/handle/321006/150957 |
| Collection | 中国科学院金属研究所 |
| Affiliation | 中国科学院金属研究所 |
| Recommended Citation GB/T 7714 | Ma Ruiting,Tian Yanwen,Zhao Haitao,et al. Synthesis, characterization and electromagnetic studies on nanocrystalline Co0.5Zn0.5Fe2O4 synthesized by polyacrylamide gel[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,2008,24(4):628-632. |
| APA | Ma Ruiting,Tian Yanwen,Zhao Haitao,Zhang Gang,&Zhao Hui.(2008).Synthesis, characterization and electromagnetic studies on nanocrystalline Co0.5Zn0.5Fe2O4 synthesized by polyacrylamide gel.JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,24(4),628-632. |
| MLA | Ma Ruiting,et al."Synthesis, characterization and electromagnetic studies on nanocrystalline Co0.5Zn0.5Fe2O4 synthesized by polyacrylamide gel".JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY 24.4(2008):628-632. |
| Files in This Item: | There are no files associated with this item. | |||||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment