	磁场辅助激光熔覆铝基金属玻璃覆层
其他题名	Aluminum-based metallic glass coatings prepared with magnetic field assisted laser cladding
	王晓明 1; 朱胜 1; 杨柏俊 2; 张垚 1; 徐安阳 1
	2018
发表期刊	航空学报
ISSN	1000-6893
卷号	39.0 期号:011 页码:422134-1
摘要	为提高铝合金的表面性能,采用磁场辅助激光熔覆的方法在5083铝合金表面制备了Al-Ni-Y-Co-La五元金属玻璃熔覆层,并对其进行组织成分及性能分析。实验结果表明：熔覆层主要由非晶相、α-Al相以及Al4NiY等金属间化合物组成,旋转磁场的搅拌作用使熔覆层非晶相含量由10.2%提高到30.7%,且能够有效抑制多道搭接和多层堆积过程中重熔区晶粒的生长,细化了熔覆层晶粒组织,降低了残余应力,提高了显微硬度及韧性,使其平均显微硬度从278HV（0.1）提高至335HV（0.1）,且波动较小,平均抗拉强度为303 MPa,为基体拉伸件的110.2%,平均伸长率为6.79%,为基体的33.1%。
其他摘要	Al-Ni-Y-Co-La five-component metallic glass cladding layer was prepared on the surface of 5083 aluminum alloy by magnetic field assisted laser cladding technology to improve the surface properties of the aluminum alloy.The microstructure and properties of the cladding layer are analised.Some of the effective experimental results show that the cladding layer is mainly composed of amorphous phase,α-Al phase and Al4 NiY intermetallic compound phase.The stirring of the rotating magnetic field increases the amorphous phase content of the cladding layer from 10.2% to 30.7% and could inhibit the recrystallization grain growth effectively in the process of multi-lap and multi-layer deposition.The residual stress is reduced and the grain structure is refined.The microhardness and tenacity are enhanced,the average microhardness increased from278 HV（0.1） to 335 HV（0.1） with less fluctuation.The average tensile strength is 303 MPa,110.2%of the matrix tensile specimen and the average elongation is 6.79%,33.1% of the matrix.
关键词	激光熔覆磁场铝基金属玻璃残余应力显微硬度抗拉强度
收录类别	CSCD
语种	中文
CSCD记录号	CSCD:6371880
引用统计	被引频次：1[CSCD] [CSCD记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/151010
专题	中国科学院金属研究所
作者单位	1.陆军装甲兵学院 2.中国科学院金属研究所
推荐引用方式 GB/T 7714	王晓明,朱胜,杨柏俊,等. 磁场辅助激光熔覆铝基金属玻璃覆层[J]. 航空学报,2018,39.0(011):422134-1.
APA	王晓明,朱胜,杨柏俊,张垚,&徐安阳.(2018).磁场辅助激光熔覆铝基金属玻璃覆层.航空学报,39.0(011),422134-1.
MLA	王晓明,et al."磁场辅助激光熔覆铝基金属玻璃覆层".航空学报 39.0.011(2018):422134-1.