Alternative TitleEffect of Cooling Rate on Boride and Room Temperature Tensile Properties of β-Solidifying γ-TiAl Alloys
王希1; 刘仁慈1; 曹如心3; 贾清1; 崔玉友1; 杨锐1
Source Publication金属学报
Other Abstractsolidifyingγ-TiAl alloys have attracted much attention for their higher specific strength and better mechanical properties at elevated temperature.They usually need some boron addition to refine the lamellar grain size,which is believed to improve their poor room temperature ductility.However,the boron addition may cause some side effects on mechanical properties for the formation of borides with unfavorable morphology and crystal structure,which is severely influenced by the alloy composition and cooling rate during casting.The components ofγ-TiAl applied usually have complex structure,such as different thicknesses,which leads to different cooling rates and therefore different microstructures and mechanical properties.To evaluate the influence of cooling rate on the microstructure and mechanical properties ofγ-TiAl investment casting,plate with step thicknesses was designed to achieve different cooling rates.Step plates ofβ-solidifying boron-containing TiAl alloy were fabricated by centrifugal casting in Y2 O3 facing coating ceramic moulds.It was found that boride mainly distributed on grain boundary,and its aspect ratio increased with increasing cooling rate,with its morphology varying from short,flat plate to long,curvy ribbon.The short plate and curvy ribbon borides were Ti B with B27 and Bfstructure,respectively.Both types of boride exhibit anisotropic growth characteristics(especially for Bfstructure),with the slowest growth rate along100and010for B27 structure and Bfstructure,respectively.This is attributed to the difficulty of atomic rearrangement along corresponding directions during solidification.The cooling rate increase caused the increase of yield strength but the decrease of room temperature ductility,the former results from the decreasing of grain size and lamellar spacing,while the latter results from the easy cracking nucleation and propagation of the long curvy boride,leaving smooth curvy surfaces on the fracture surface.Samples containing short flat plate boride showed better ductility,and no smooth curvy surface was observed.
Keywordγ-TiAl合金 β凝固 熔模铸造 冷却速率 硼化物 拉伸性能
Indexed ByCSCD
Citation statistics
Cited Times:1[CSCD]   [CSCD Record]
Document Type期刊论文
Recommended Citation
GB/T 7714
王希,刘仁慈,曹如心,等. 冷却速率对β凝固γ-TiAl合金硼化物和室温拉伸性能的影响[J]. 金属学报,2020,000(002):203-211.
APA 王希,刘仁慈,曹如心,贾清,崔玉友,&杨锐.(2020).冷却速率对β凝固γ-TiAl合金硼化物和室温拉伸性能的影响.金属学报,000(002),203-211.
MLA 王希,et al."冷却速率对β凝固γ-TiAl合金硼化物和室温拉伸性能的影响".金属学报 000.002(2020):203-211.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[王希]'s Articles
[刘仁慈]'s Articles
[曹如心]'s Articles
Baidu academic
Similar articles in Baidu academic
[王希]'s Articles
[刘仁慈]'s Articles
[曹如心]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[王希]'s Articles
[刘仁慈]'s Articles
[曹如心]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.